Abstract:Cu/MgO-Al2O3 (Mg/Al atomic ratio=1/1, 3/1, 4/1), Cu/MgO and Cu/Al2O3 catalysts with high Cu dispersions were prepared by an impregnation method using ethanol as solvent instead of water. Compared to water, ethanol as solvent was favorable not only for obtaining the high dispersions of the Cu clusters on the basic oxide supports, but also for retaining the basicity and structures of the supports during the catalyst preparation. The density of the basic sites for the dispersed Cu catalysts increased with increasing the MgO contents in the basic supports. These catalysts catalyzed glycerol hydrogenolysis to propylene glycol with a high selectivity (>90%), and showed slight deactivation in dioxane at 200 degrees C and 6.0 MPa H-2. Their reaction rates normalized by per exposed Cu atom increased with increasing the ratios of the basic sites to Cu atoms on the catalyst surfaces. The intrinsic hydrogenolysis activity of the Cu atoms were probed by N2O chemisorption-H-2 temperature programmed reduction, which did not change essentially with the Cu loadings (2-6 wt%) and the Mg/Al atomic ratios of the MgO-Al2O3 supports. Meanwhile, the basic sites alone on the supports were inactive for the glycerol conversion. Taken together, we propose a synergetic effect that the basic sites at the interfaces between the Cu sites and the supports assist the cleavage of alpha-C-H bonds of glycerol on the Cu surfaces leading to the faster dehydrogenation of glycerol to glyceraldehyde, a kinetically-relevant step in glycerol hydrogenolysis to propylene glycol. These active basic sites appear to be the Bronsted OH- sites, i.e. the hydroxyl groups bonded to the surface Mg2+ cations on MgO-Al2O3. The understanding on such synergy between the basic sites and Cu sites in glycerol hydrogenolysis provides a basis for the rational design of superior hydrogenolysis catalysts and selective removal of oxygen from biomass-derived feedstocks.

Synergistic effects on Cu, Zn and Al-based catalyst: tracking the change of active sites during glycerol dehydration

Structure-reactivity relations in Cu/ZrO2 catalysed glycerol dehydration to acetol in continuous flow system

Dehydration of Glycerol to Acrolein over Hierarchical ZSM-5 Zeolites: Effects of Mesoporosity and Acidity

Microwave-assisted Catalytic Dehydration of Glycerol for Sustainable Production of Acrolein over a Microwave Absorbing Catalyst

Regulation of Pore Structure and Acidity of a ZSM-5 Catalyst for Dehydration of Glycerol to Acrolein

Insight into the Effect of Cu Species and Its Origin in Pt-Based Catalysts on Reaction Pathways of Glycerol Oxidation

Vapor-phase dehydration of glycerol to acetol over Cu/SiO 2 prepared with organic additives

Selective Hydrogenolysis of Glycerol to Propylene Glycol on MgO-Al2O3Dispersed Cu Catalysts

Effect of support for alcohol-hydrocarbon synthesis from syngas in Cu-based catalyst

Synergy between Active Sites of Ternary CuZnAlOOH Catalysts in CO Hydrogenation to Ethanol and Higher Alcohols

Glycerol Valorization over ZrO2-Supported Copper Nanoparticles Catalysts Prepared by Chemical Reduction Method

Sustainable production of acrolein: effects of reaction variables, modifiers doping and ZrO2 origin on the performance of WO3/ZrO2 catalyst for the gas-phase dehydration of glycerol

Photo-Chemically-Deposited and Industrial Cu/ZnO/Al2O3 Catalyst Material Surface Structures During CO2 Hydrogenation to Methanol: EXAFS, XANES and XPS Analyses of Phases After Oxidation, Reduction, and Reaction

Catalytic Dehydration of Glycerol to Acrolein over Short B-Axis H-ZSM-5

Gas Phase Dehydration of Glycerol to Acrolein Over NaHSO4@Zr-MCM-41 Catalyst

Synergistic Effects of Nonthermal Plasma and Solid Acid Catalysts in Thermo-Catalytic Glycerol Dehydration

Self-Pillared MFI-Type Zeolite Nanosheets As Selective Catalysts for Glycerol Dehydration to Acrolein

Mildly Acidic Aluminosilicate Catalysts for Stable Performance in Ethanol Dehydration

Preparation of Highly Dispersed Cu Catalysts from Hydrotalcite Precursor for the Dehydrogenation of 1,4-Butanediol

Effects on structure by spectroscopic investigations, valence state and morphology properties of FeCo-containing SnO 2 catalysts for glycerol valorization to cyclic acetals