Insight into the Hot Corrosion Behavior of FeMnCrSi/TiC Coatings at 900 °C

Xu Tang,Lei Li,Ze Huang,Jieji Zhou,Yonghuang Qin,Shiyang Zhao,Da Liu,Zhengbing Xu,Jianmin Zeng,Hongqun Tang,Youbin Wang

DOI: https://doi.org/10.3390/met14050504

IF: 2.695

2024-04-27

Metals

Abstract:This study explores the deposition of an Fe-MnCrSi/TiC coating on 45 steel surfaces using high-velocity arc spraying technology, examining the microstructure and hot corrosion behavior of the resultant layer. The microstructure of the FeMnCrSi/TiC coating primarily consists of an α-Fe (BCC) solid solution, composed of Fe, Mn, Cr, Si, C, and other elements, with a minor presence of β-Fe (FCC) solid-solution phase and unmelted TiC particles. Following 100 h of cyclic 900 °C hot corrosion, Mn on the coating surface preferentially oxidizes, forming a manganese-rich oxide layer. This process reduces the oxygen partial pressure (O2) within the coating, prompting the formation of a dense Cr2O3 layer on the inner side of the oxide layer. Concurrently, the rapid diffusion of Mn and Cr elements triggers the generation of Mn- and Cr-deficient regions at the metal/oxide layer interface, inducing the transformation of the coated metal primary matrix from an FCC + BCC dual phase to an α-Fe (BCC) single phase. After the reaction, the hot corrosion weight gain of the coating reached 12.43 mg/cm2, approximately one-fourteenth of the weight gain of the 45 steel substrates. This weight gain adheres to the parabolic law, suggesting that the FeMnCrSi/TiC coating exhibits excellent corrosion resistance under the given conditions.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper aims to study the hot corrosion behavior of FeMnCrSi/TiC coatings at 900°C. Specifically, the research prepared FeMnCrSi/TiC coatings on the surface of 45 steel using High Velocity Arc Spraying (HVAS) technology and conducted a detailed analysis of their microstructure and hot corrosion performance. The main objective is to evaluate the corrosion resistance of this coating under high-temperature conditions and to explore its potential anti-corrosion mechanisms.

The study found that after 100 hours of cyclic hot corrosion, the manganese element on the coating surface preferentially oxidized to form a manganese-rich oxide layer, which reduced the oxygen partial pressure within the coating and promoted the formation of a dense Cr2O3 layer internally. Meanwhile, the rapid diffusion of manganese and chromium elements led to the appearance of manganese and chromium-deficient regions at the metal/oxide layer interface, causing the coating matrix to transform from an FCC+BCC dual phase to an α-Fe (BCC) single phase. Ultimately, the hot corrosion weight gain of the coating reached 12.43 mg/cm², which is only about one-fourteenth of the weight gain of the uncoated 45 steel substrate. Additionally, the hot corrosion weight gain of the coating followed a parabolic law, indicating that the FeMnCrSi/TiC coating exhibits excellent corrosion resistance under the given conditions.