Effect of microwave curing on the properties of aggregate-mastic interfacial transition zones in cement emulsified bitumen mixture containing steel slag

Kuo Ji,Yaogang Tian,Jing Jiang,Xiaohui Yan,Jin Tian,Zhenjun Wang,Jun Zhang,Kan Jia

DOI: https://doi.org/10.1016/j.mtcomm.2024.109481

IF: 3.8

2024-06-09

Materials Today Communications

Abstract:The poor properties of the aggregate-mastic interfacial transition zones (ITZ) are the core factor for the low structural strength of cement emulsified bitumen mixture (CEBM), while incorporating steel slag with high microwave responsiveness into CEBM and followed by microwave curing may be an effective method to enhance ITZ properties. To verify this hypothesis, the ITZ properties of CEBM containing steel slag were characterised and analysed by a series of techniques such as Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), and nanoindentation. The results showed that the ITZ properties increased continuously with microwave curing time. Specifically, the thickness of ITZ continuously decreased, while the elastic modulus and hardness continuously increased. When the microwave curing time was less than 7 min, the growth in cement hydrates and temperature simultaneously enhanced the ITZ properties. When the microwave curing time exceeded 7 min, the cement hydrates gradually decreased due to the water content falling below the minimum required for cement hydration, and the improvement of ITZ properties mainly depended on the temperature rise. Remarkably, the microwave heating characteristics of steel slag resulted in a tighter bond with bitumen, which led to consistently better surface ITZ properties than limestone. However, it should be avoided that the microwave curing time is too long, as this would result in the steel slag temperature being too high and aging its surface bitumen. Additionally, the indirect tensile strength of CEBM affected by the ITZ properties was still increased even after the decrease in cement hydrates.

materials science, multidisciplinary