Polyethylene Glycol/Rice Husk Ash Shape-Stabilized Phase Change Materials: Recovery of Thermal Energy Storage Efficacy via Engineering Porous Support Structure

Giang Tien Nguyen,Bui Van Phuoc,Tran Thi Nhung,Le Thi Duy Hanh,Huynh Nguyen Anh Tuan,Ly Tan Nhiem
DOI: https://doi.org/10.1021/acsomega.3c09417
IF: 4.1
2024-04-23
ACS Omega
Abstract:This study focuses on modifying the porous structure of acid-treated rice husk ash (ARHA) to enhance the thermal energy storage capacity of poly(ethylene glycol) (PEG) confined within shape-stabilized phase change materials. The modification process involved a cost-effective sol-gel method in which ARHA was initially dissolved in an alkaline solution and subsequently precipitated in an acidic environment. ARHA, being a mesoporous SiO(2)-based material with a high surface area but low pore...
chemistry, multidisciplinary
What problem does this paper attempt to address?
### Problems the Paper Attempts to Solve This paper aims to improve the thermal energy storage performance of polyethylene glycol (PEG) in shape-stable phase change materials by enhancing the porous structure of acid-treated rice husk ash (ARHA). Specifically, the authors employed a simple and cost-effective sol-gel method to modify the structure of ARHA, resulting in modified ARHA (mARHA) with a three-dimensional macroporous network structure. This improvement aims to address the following key issues: 1. **Low Adsorption Capacity**: The original ARHA, due to its low pore volume (0.28 cm³/g), can only adsorb 50% of PEG, limiting its application in thermal energy storage. 2. **Crystallinity Suppression**: The high specific surface area of ARHA (158 m²/g) leads to the formation of numerous interfacial hydrogen bonds with PEG, suppressing the crystallinity of PEG and thereby reducing thermal energy storage efficiency. 3. **Insufficient Thermal Performance**: Due to the aforementioned issues, the thermal energy storage capacity of PEG/ARHA composites is only 0 J/g, which is inadequate for practical applications. Through structural modification, mARHA not only increased the adsorption capacity of PEG to 70% but also significantly improved the crystallinity of PEG, enhancing the thermal energy storage capacity from 0 J/g to 109.3 J/g. Additionally, mARHA exhibited higher thermal conductivity, thermal stability, and reliability, making it suitable for large-scale applications such as building energy efficiency.