Spontaneous-reduction and photoluminescence tuning in singly-doped Ba5-Ca (PO4)3Cl:Eu2+/Eu3+ phosphors
Peng Wang,Jiashan Mao,Xiantao Wei,Liting Qiu,Bin Jiang,Fengfeng Chi,Min Yin,Yonghu Chen
DOI: https://doi.org/10.1016/j.jallcom.2021.159277
IF: 6.2
2021-07-01
Journal of Alloys and Compounds
Abstract:Developing a feasible scheme for solid-state lighting with high-quality white light remains a significant challenge. Particularly, tunable luminescence with single-component white emission have been widely studied to improve the luminescence performance of phosphor-converted white light-emitting diodes (pc-WLEDs) phosphors. In this work, a novel spontaneous reduction phenomenon was first found in Eu-activated apatite-type Ba5(PO4)3Cl phosphors prepared by a solid-phase reaction in air. Under 362 nm excitation, the luminescence results showed that a broad blue Eu2+ emission band with a peak at 437 nm appears unexpectedly in addition to the usual sharp orange-red emission of Eu3+. The mixed-valence fact of Eu2+/Eu3+ was further confirmed by X-ray photoelectron spectra and time-resolved spectroscopy techniques. The underlying mechanism could be explained by a charge compensation model. Accordingly, the local crystal-site engineering control of the luminescence in Ba5-y Ca y (PO4)3Cl:Eu2+/Eu3+ had been studied in detail by the introduction of Ca2+. It is found that the Ca2+ substitution of Ba2+ will lead to new splitting peaks of Eu3+ emission and a red-shift followed by a blue-shift of Eu2+ emission respectively, which could eventually adjust the luminescence of phosphors to the proper white light region. These phenomena are mainly ascribed to the introduction of Ca2+ to the structure modification of activator coordination environment. Finally, based on the thermal quenching results indicate that the potential application of the single-doped mixed-valence phosphor system in pc-WLEDs.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering