Abstract:Phosphogypsum (PG) is a kind of industrial solid waste with high impurity content and low utilization rate. In this study, α-hemihydrate gypsum (α-HH) was synthesized from PG in H3PO4–H2O solution (wet-process phosphoric acid solution and phosphoric acid solution) under atmospheric pressure. The crystal morphology of α-HH was controlled by adding F and Al compound regulators, and the mechanical properties of α-HH were improved. The difference of α-HH synthesized by PG with different qualities was analyzed, and the mechanism of α-HH morphology was studied by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and energy-dispersive spectroscopy (EDS). Results showed that in the wet-process phosphoric acid solution, α-HH synthesized from white PG (by H3PO4–H2SO4 two-step method) had better whiteness, purity, and mechanical properties compared with that from industrial PG, and the performance indexes of the α-HH products met the requirements of α50 grade in JC/T 2038–2010 α-high-strength gypsum in China and have a good commercial application prospect. Moreover, in the phosphoric acid solution, the average diameter of the α-HH crystal increased from 8.1 µm to 54.8 µm, the average aspect (L/D) ratio decreased from 32.65 to 0.52, and the induction period and growth period of the α-HH crystal were prolonged with the increase in regulator dosage. F− and Al3+ ions were preferred to adsorb on the crystal faces. The growth of the crystal parallel to c-axis (200), (020), and (400) was inhibited, and the morphology of the α-HH crystal changed from whisker to short column. When the dosage of the regulator was 1.1 %, the 2 h bending strength of the α-HH product was 6.56 MPa, and the drying compressive strength was 52.4 MPa. This study provides a new technique and method for the synthesis of high-strength α-HH products from PG.

Hydration Mechanism and Hardening Property of α-Hemihydrate Phosphogypsum

Hydration Mechanism and Hardening Property of α-Hemihydrate Phosphogypsum

L-aspartic acid: A crystal modifier for preparation of hemihydrate from phosphogypsum in CaCl2 solution

Enhancing the hydration reactivity of hemi-hydrate phosphogypsum through a morphology-controlled preparation technology

Facile Preparation of High-Strength Α-Caso 4 ·0.5H 2 O Regulated by Maleic Acid from Phosphogypsum: Experimental and Molecular Dynamics Simulation Studies

Hydration reaction and microstructural characteristics of hemihydrate phosphogypsum with variable pH

Utilization of phosphogypsum to synthesize α-hemihydrate gypsum in H3PO4–H2O solution

Facile preparation of high-strength α-CaSO4·0.5H2O regulated by maleic acid from phosphogypsum: experimental and molecular dynamics simulation studies

Effect of Soluble Phosphorus on the Mechanical Properties of α-Hemihydrate Gypsum

Influence mechanism of alkaline environment on the hydration of hemihydrate phosphogypsum: A comparative study of various alkali

Effect of Soluble P2O5 Form on the Hydration and Hardening of Hemihydrate Phosphogypsum

Coordinated disposal of FGD gypsum and power plant concentrated brine via preparation of α-hemihydrate gypsum

Impact of carboxylic acid structure on α-hemihydrate gypsum crystal morphology and mechanical strength

Influence of crystal modifier on the preparation of α-hemihydrate gypsum from phosphogypsum

Effect of modifiers on crystalizing habit and mechanical strength of α-hemihydrate gypsum prepared from PG by an autoclaved method

Trace NaCl and Na2EDTA Mediated Synthesis of Α-Calcium Sulfate Hemihydrate in Glycerol–Water Solution

Preparation of α-hemihydrate gypsum from phosphogypsum in glycerol and Na2SO4 mixed solutions under atmospheric pressure

Study on physical and chemical characteristics of β-hemihydrate phosphogypsum