The effect of laser cleaning on metallurgical properties and intergranular corrosion behavior of 304 stainless steel

Ali Hadipour,Mohammad Ghasem Gholami,Mohammad Reza Hosseini
DOI: https://doi.org/10.1016/j.mtcomm.2024.111104
IF: 3.8
2024-11-29
Materials Today Communications
Abstract:One of the strong possibilities of 304 stainless steel used in the industry is susceptibility to intergranular corrosion. The main purpose of this study is to investigate the effect of the laser cleaning process on the intergranular corrosion of this material. In this paper, 304 stainless steel plates were subjected to laser scanning under four power densities of 3.18×10 6 , 4.77×10 6 , 6.36×10 6 , and 7.96×10 6 W/cm 2 , and then sensitized for 4 h at a temperature of 750 oC. According to practice A in ASTM A262 standard, ditch marks around the grain boundaries were observed in all lasered samples. As a result of bending samples at an angle of 180o according to practice E in ASTM A262 standard, no cracks were observed in the bending area. By performing the ISO 12732 standard, it was found that the ratio of I r /I a in all lasered samples was higher than 0.05 and the samples were sensitive to intergranular corrosion, quantitively. A smaller dimension of average grain size was created in the sample lasered at a power density of 4.77×10 6 W/cm 2 . In addition, in this sample, the preferred texture of the (220) plane as a non-compressed (220) plane was also observed. Among the lasered samples, this sample had a higher uniform corrosion resistance and achieved a resistance of R ox =78.3 kΩ.cm 2 . Despite the qualitative approval of the samples (according to ASTM A262, practice E) and their quantitative rejection (according to ISO 12732) regarding the intergranular corrosion, it was suggested to use a power density of 4.77×10 6 W/cm 2 in the case of laser cleaning operations in areas where the laser beam may hit the 304 stainless steel substrates.
materials science, multidisciplinary
What problem does this paper attempt to address?