Preparation and evaluation of Pingyangmycin-loaded chitosan thermogels for vascular malformations therapy
Fen Chen,Weisan Pan,Xingjun Qin
2014-01-01
Abstract:SUMMARY The purpose of our study was to investigate the potential of Pingyangmycin (PYM) -loaded chitosan (CS) thermogels for interventional embolization therapy. PYM-CS thermogels were prepared and evaluated by the rheological properties and in vitro release behaviors. Rheological studies proved that as the temperature raised to about 37°C , the PYM thermogels transformed from solution phase to gel phase. It was showed that in vitro release of PYM from the thermogels could be delayed up to 10 days. INTRODUCTION Chemoembolization, which connects the benefits of therapeutic drugs and embolic materials, has become a promising therapy for vascular malformations. However, few reports have been concerned about the connected use of sclerosants and embolic materials. The purpose of our study was to obtain an infarction effect and a sustained therapeutic effect by decrease of blood flow through the sclerosis effect and delayed release behavior of the chitosan (CS) thermogels. CS thermogels with suitable strength could decrease or even cut off the blood flow and the sclerosants release from thermogels can induce the proliferation and migration of vascular cells and thus thickening of the vessel wall which finally result in the occlusion of the vessels. Pingyangmycin (PYM), which is a new type of cytotoxic glycopeptide antitumor antibiotic and was developed in China in the 1980’s, has been used extensively in the far East for treatment of head and neck tumors with a definite therapeutic effect was selected as a model sclerosant.1 However, short half-life and lung-toxicity restrained its further application in clinic.2 So, in present study, CS thermogels were chosen as carrier matrix due to its good biocompatibility, and then PYM-CS thermogels were prepared and played dual roles as sclerosants and embolic materials. EXPERIMENTAL METHODS Preparation of PYM-CS thermogels was as follows: typically, CS (1.8%-2.2%, w/v) was added slowly to 0.1 mol/l acetic acid with stirring, and then the mixture was continuously stirred overnight to make a clear solution. Then the CS solution was chilled to 4°C in an ice bath. Glycerophosphate (GP) (6%-14%, w/v) and PYM (2mg/ml-4mg/ml) were dissolved in purified water separately, and chilled along with the CS solution to 4°C . The GP solution was added dropwise into the CS solution with agitating and then they were mixed for 10 min. Finally, the formulation was obtained by adding PYM solution to the CS-GP solution under stirring for 6 min. The rheology study was carried out on AR2000ex rheometer (TA. Co. Ltd., USA) equipped with a 40mm parallel plate rotor and 5ml formulation sample was needed. In variable temperature mode, the changes in elastic modulus (G’) and loss modulus (G’’) were recorded as a function of temperature. The oscillatory frequency was fixed at 1.0 Hz during the measurements. The temperature changed from 15°C to 45°C with a rate of 2°C/min. In the study of in vitro release, 3ml of the PYM-CS thermogels were injected into 20ml glass vials (diameter 20mm) and then kept warm in an 37°C water bath for half an hour so that they could be transformed into gel completely. Then 15ml phosphate buffer solution (pH7.4) (PBS) containing NaN3 (0.05%, w/v) and lysozyme (1.0%, w/v) were added into the vials. The dissolution system was shaken in an incubator at 50rpm and 37°C . The release medium was all collected at predetermined time intervals for analysis and replaced with same amount of fresh dissolution medium. The concentration of PYM in the release medium was assayed by a high performance liquid chromatography (HPLC) method. All the in vitro dissolution tests were carried out in triplicate, and the accumulation release amount of PYM from PYM-CS thermogels was calculated. RESULTS AND DISCUSSION The morphology of the PYM-CS thermogels before and after sol-gel transition was displayed in Fig.1. It was showed that the formulations, which were transformed from solution to gel with the increase of temperature, had good thermosensitive properties. Fig.1 Picture of the PYM-CS thermogels before and after