Abstract:In a previous publication [Macromolecules2019,52, 5245–5254], we described the synthesis of surfactant-free latex dispersions of nanoparticles (NPs) based on emulsification of a preformed proprietary BASF polymer (MnGPC = 5000 g/mol, D̵ = 3), in which the −COOH groups were partially neutralized by using ammonia. The NPs in these dispersions were then partially cross-linked with neopentyl glycol diglycidyl ether (NGDE) to increase the molecular weight, followed by reaction with monoglycidyl ether to reduce the acid number and lower the glass transition temperature (Tg). In the work reported here, we used fluorescence resonance energy transfer (FRET) measurements to examine polymer diffusion rates in the films formed from these dispersions. We compared films formed from the uncross-linked NPs, with ones containing the NPs partially cross-linked with NGDE but not reacted with the monoepoxide. In this way, both the cross-linked and noncross-linked polymers had similar Tg values. We also examined films formed from a similar polymer with MnGPC = 4000 g/mol, D̵ = 3. Because of the high Tg of these polymers (ca. 65 °C), films were formed on heated substrates, and this led to skin formation at the film surface. We used FRET measurements to monitor the extent of polymer diffusion at both the film–air (F–A) and film–substrate (F–S) interfaces. We found that the onset of polymer diffusion occurred more rapidly within the skin at the F–A interface at elevated temperatures, but this was quickly surpassed by polymer diffusion at the bottom of the film because of the hydroplasticization effect. The presence of the skin layer retarded water evaporation and extended the time needed for the efficiency of energy transfer to reach its plateau value. We also found that the extent of chain diffusion in the partially cross-linked (XL) films was reduced compared to the non-XL samples because of limited interdiffusion of the polymer that formed the gel content. Dynamic mechanical analysis was employed to investigate the viscoelastic behavior of the samples using time–temperature superposition to generate master curves. We calculated apparent activation energies in the temperature range of the FRET experiments that were consistent with the strong dependence of polymer diffusion rates on the difference between the annealing temperature and glass transition temperature.

Vegetable oil hybrid films cross-linked at the air-water interface: formation kinetics and physical characterization

Synergistic impact of natural gums and crosslinkers on the properties of oilseed meals based biopolymeric films

A hybrid approach to oil structuring – combining wax oleogels and capillary suspensions

Characterization of Gelatin-Based Edible Films Incorporated with Olive Oil

Biopolymers from vegetable oils via catalyst- and solvent-free "click" chemistry: effects of cross-linking density

Preparation of films based on reticulated fish gelatin containing garlic essential oil

Molecular Aspects of Film Formation of Partially Cross-Linked Water-Borne Secondary Dispersions that Show Skin Formation upon Drying

Effect of Homogenization Conditions on Properties of Gelatin–olive Oil Composite Films

Vegetable oil‐based thermosetting polymers

Self-Healable Hydrogels from Vegetable Oil: Preparation, Mechanism, and Applications

Development and structural assessment of whey protein isolate/sunflower seed oil biocomposite film

Effect of Homogenization on Physical and Controlled Release Properties of Gelatin Emulsion Films

A Solvent-Free Approach to Crosslinked Hydrophobic Polymeric Coatings on Paper Using Vegetable Oil

Structural and physico-mechanical properties of potato starch-olive oil edible films reinforced with zein nanoparticles

Citric acid crosslinked ternary blended (polyvinyl alcohol, lignin, lemongrass essential oil/nanoemulsions) biopolymeric hydrogel films: structural, functional, antioxidant, antifungal and biodegradable properties

Optimization of a Solvent Exchange Method Enabling the Use of Dehydrated Cellulose Nanofibers as the Thickener in Lubricating Oleogels

Development of Multifunctional Hybrid Coatings (Mechanically Resistant and Hydrophobic) Using Methyltrimethoxysilane–Diethoxydimethylsilane–Tetraethoxysilane Mixed Systems

"Thiol-Ene" Photo-Cured Hybrid Materials Based on Poss and Renewable Vegetable Oil

Hydroxypropyl Cellulose Films Filled with Halloysite Nanotubes/Wax Hybrid Microspheres

Lignin-Polylactide Reverse Emulsions for Water and UV-Resistant Composite Films

Organic–Inorganic Hybrid Materials from Vegetable Oils