Macro-encapsulation of metal balls prepared by waste aluminum cans in ceramic capsules with reserved space

Qiulin Xia,Meijie Zhang,Huazhi Gu,Mweemba Stephen,Chengliang Ye,Haifeng Li,Xing Liu

DOI: https://doi.org/10.1016/j.ceramint.2023.02.135

IF: 5.532

2023-06-01

Ceramics International

Abstract:Phase change materials (PCMs) form the core of thermal energy storage (TES) for enhancing solar and industrial waste heat recovery. Metals have attracted growing attention due to their unique advantages, including high latent heat storage and high thermal conductivity. The application of metallic PCMs in TES is limited by the absence of appropriate packaging technology. Volume expansion during the solid-liquid phase can cause breakage of the protective coatings. This study proposes a “double-layer coating, recycling inner layer” method for the encapsulation of metallic PCMs. Waste aluminum cans (WACs) were selected as the PCM for cost reasons. The alloy balls prepared using the WACs were sequentially coated with an alkane mixture and ceramic slurry. The alkane mixture melts and discharges during the baking process, leaving a void for the phase-change volume expansion. The shell was gradually densified, and the metallic PCM was completely encapsulated after the heat treatment. The prepared MAEPCMs heat-treated at 1200 °C showed excellent mechanical properties, high heat storage capacity, and thermal cycle stability. The force required for compressive failure was approximately 2623 N. In addition, the total heat storage capacity reached approximately 198.6 kJ/kg at the temperature range of 600–700 °C, of which the latent heat accounted for more than 98.5%. There was no erosion between the alloy and the shell material, and the cumulative mass change was less than 8 wt. % after 600 thermal cycles. This study provides a structurally stable and low-cost technique for the preparation of durable macro-encapsulated PCMs with a high heat storage capacity and high thermal conductivity.

materials science, ceramics