Half-sectioned spot weld parameter optimisation for liquid metal embrittlement analysis in advanced high-strength steels

J U Kim,M Shojaee,O Sherepenko,D Ramachandran,O T Betiku,A R H Midawi,H Ghassemi-Armaki,E Biro

DOI: https://doi.org/10.1177/13621718231222844

2024-01-17

Abstract:Half-section welding has been proposed as a method to observe nugget growth throughout the resistance spot welding process. Some past studies used this technique as an in-situ monitoring approach to analyse the cracking behaviour during welding. However, there is a lack of understanding regarding the half-sectioned welding parameters, which critically impacts the liquid metal embrittlement cracking index. This study optimised half-sectioned welding parameters for liquid metal embrittlement crack analysis by developing process maps that compare the half-sectioned and full-section processes. It was found that the liquid metal embrittlement crack located at the weld shoulder can correlate to the temperature gradient in the heat-affected zone. This study proposes half-sectioned welding as a viable technique for liquid metal embrittlement analysis.

materials science, multidisciplinary,metallurgy & metallurgical engineering