Abstract:Novel Fe35Ni20Cr20-xCoxMo5P12C4B4 (x = 0, 4,8, 12, 16 in at.%, denoted as Cr20-xCoxMo5) high-entropy bulk metallic glasses (HE-BMGs) with excellent comprehensive performance were successfully fabricated using Fluxing and J-quenching methods. The focus was on studying the influences of different Co content on the glass-forming ability (GFA), mechanical performances, magnetic properties, and anti-corrosion performance. It was found that adding an appropriate amount of Co to replace Cr in Cr20-xCoxMo5 alloys can improve GFA. The Cr12Co8Mo5 specimen displays the maximum critical diameter of 3.5 mm and maximum super-cooled liquid phase of 51 K. The compression tests show that the plasticity was enhanced from 0.2 % for the Co-free alloy to 2.5 % for the 12 at.% Co-added alloy. The saturation magnetization (J s) of Cr20-xCoxMo5 alloys gradually increased from 0.04 to 0.68 T with the increase of Co. Electrochemical tests indicate that in 3.5 wt.% NaCl solution at room-temperature (RT), the anti-corrosion performance of Cr20-xCoxMo5 alloys expresses a trend of first increasing and then decreasing with the increase of Co, and all samples show a remarkably higher anti-corrosion performance than 316 L and 304 L stainless steel. The Cr16Co4Mo5 sample exhibits the highest anti-corrosion performance with the self-corrosion current density (I corr) and the self-corrosion potential (E corr) are 9.5 × 10−9 A/cm2 and -0.270 V, respectively. The X-ray photoelectron spectroscopy (XPS) analysis of the Cr16Co4Mo5 shows that there is a higher content of metal kation oxides of Fe2+, Cr3+ and Mo4+ in the passive films compared to Cr20Mo5 and Cr4Co16Mo5. It is indicated that the Cr16Co4Mo5 specimen has the optimal corrosion resistance in this current research. The present HE-BMGs have high GFA, high plastic strain,and excellent anti-corrosion performance, which have potential application value in the engineering field.

Effect of Ni addition on the properties of CoMoPB bulk metallic glasses

Preparation and properties of new non-magnetic Co-based bulk metallic glasses

Ductile Ni-based bulk metallic glasses at room temperature

Effects of Ni Substitution for Fe/Co on Mechanical and Magnetic Properties of Co-based Bulk Metallic Glasses

Thermal, magnetic and mechanical properties of (Fe 1 − x Co x ) 68 Dy 6 B 22 Nb 4 bulk metallic glasses

Effect of partial substitution of Cr with Co on the properties of Fe35Ni20Cr20-xCoxMo5P12C4B4 high-entropy bulk metallic glasses

Effect of Cr/Mo content on the properties of transition-metal based high entropy bulk metallic glasses

Effects of Cu Additions on Mechanical and Soft-Magnetic Properties of CoFeBSiNb Bulk Metallic Glasses

Effect of partial substitution of Cr with Co on glass forming ability, mechanical and magnetic properties in Fe48Mo14Cr15-xCoxB6P8Si7Y2 bulk metallic glasses

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses

Improved glass forming ability and soft magnetic properties by minor Mo alloying in Fe–P–C–B–Si bulk metallic glasses

Effect of Nb Addition on the Glass-Forming Ability, Soft-Magnetic Properties and Mechanical Properties of CoFeNiBSiNb Bulk Glassy Alloys

[Ni-Mo-Si]:Nb Bulk Metallic Glasses: Microstructure, Mechanical and Corrosion Studies

Effects of B/P and Co/Fe substitutions on glass-forming ability and soft magnetic properties of a Fe80P13C7 metallic glass

Ductile Co-based Bulk Metallic Glass with Superhigh Strength and Excellent Soft Magnetic Properties Induced by Modulation of Structural Heterogeneity

Effects of Mo on the Glass Forming Ability and Properties of Fe-B-C-P-Si-Mo Bulk Metallic Glasses

Effects and mechanisms of Nb and Fe additions on glass-forming ability and magnetic properties of a Co71.5Gd3.5B25 metallic glass

Co-Based Bulk Metallic Glasses with Good Soft-Magnetic Properties and High Strength

Enhancement of glass-forming ability and thermal stability of a soft magnetic Co75B25 metallic glass by micro-alloying Y and Nb

Effects of Co Substitution for Fe on the Glass Forming Ability and Properties of Fe80P13C7 Bulk Metallic Glasses

Role of Fe substitution for Co on thermal stability and glass-forming ability of soft magnetic Co-based Co-Fe-B-P-C metallic glasses