Abstract:Shield method have been commonly used in water conveyance tunnels. To improve the bearing capacity of a shield tunnel under internal water pressure, a reinforced concrete lining is constructed inside the segmental linings to form a composite lining structure. However, cracks typically occur in reinforced concrete inner linings. In this study, a prototype test was performed to investigate the failure process of a composite lining. Based on the test observations, the progressive failure process of the composite lining experienced four stages. In the elastic stage, the stress and deformation of the composite lining increased linearly with the internal pressure, and no cracks appeared. In the cracking stage, cracks first occurred in the inner lining near the joints and were subsequently uniformly distributed along the circumferential direction. In the joint damage stage, the cracking of the inner lining caused more internal pressure to transmit to the segmental lining. As the internal pressure increased, compressive damage occurred in the handholes of the segmental joints. Finally, in the failure stage, the damage to the joints deteriorated and more internal pressure was borne by the rebar of the inner lining. Shear failure typically occurred at the welding point of the inner-lining rebar, followed by joint fracture near the welding point. Finally, the composite lining lost its ability. The test results showed that cracking of reinforced concrete inner lining remarkably decreased the tensile stiffness of composite lining. Consequently, the joint opening and convergence of the tunnel developed at a higher rate, posing a threat to the operational safety of the tunnel. The tensile stiffness is a key factor related to the deformation and bearing capacity of a shield tunnel. Therefore, an analytical solution was established to calculate the tensile stiffness of the composite lining after cracking. The analytical solution matched the test results well. In addition, the effects of the thickness and reinforcement ratio of the inner lining were analysed. The results suggested that increasing the reinforcement was more beneficial in improving the tensile stiffness of the composite lining.

Full-scale experimental investigation on progressive failure characteristics of shield segmental lining connected through segmental joints containing ductile-iron joint panels

Full-scale Loading Test for Shield Tunnel Segments: Load-bearing Performance and Failure Patterns of Lining Structures

Interface Failure of Segmental Tunnel Lining Strengthened with Steel Plates Based on Fracture Mechanics

Full-scale experiment for segmental linings of deep-buried shield tunnels bearing high inner water pressure: Comparison of mechanical behaviors of continuous- and stagger-jointed structures

Analytical Method for Segmental Tunnel Linings Reinforced by Secondary Lining Considering Interfacial Slippage and Detachment

Observed response of a shield-driven tunnel to fluctuations in river stage

Failure process and tensile stiffness of shield tunnel with reinforced concrete inner lining under internal water pressure

Full-Scale Experimental Study on the Effect of Ground Surcharge on the Stress and Deformation of Shield Tunnels

Study on Mechanical Characteristics of Segmental Joints of a Large-Diameter Shield Tunnel under Ultrahigh Water Pressure

Full-scale Experimental and Structural Characterization Study of Shield Tunnel Reinforcement under Ground Stacking Loads

Structural Behavior of Triple-Layer Composite Lining of a Water Conveyance Tunnel: Insight from Full-Scale Loading Tests

Experiments and Numerical Simulation of the Reinforcement Effect of Channel-Steel-reinforced Shield Tunnel Segments under Unloading Conditions

Influence of the Diameter Size on the Deformation and Failure Mechanism of Shield Precast Segmental Tunnel Lining under the Same Burial Depth

Full-scale experiment on the bearing and deformation characteristics for prestressed double-layered shield tunnel linings under high internal pressure

Experimental study on the high water pressure erosion mechanism and its influence on the submarine shield tunnel concrete segments

Mechanical Analysis of Segment Floating During Shield Tunnel Construction

Numerical study on mechanical behavior and ultimate bearing capacity of shield segment joints under different load conditions

Structural responses and treatments of shield tunnel due to leakage: A case study

Full scale tests and a progressive failure model to simulate full mechanical behavior of concrete tunnel segmental lining joints

Fluid-solid coupling response of shield tunnel lining structure under high water pressure

Study on Lining Mechanical Behavior of Super Large Diameter Shield Tunnel during Segment Opening