Long-term polarization accelerated degradation of nano-thin C/Ti coated SS316L bipolar plates used in polymer electrolyte membrane fuel cells

Xian-Zong Wang,Meng-Meng Zhang,Dong-Dong Shi,Shang-Chen Zhang,Yuan-Min Wu,Wei-Jia Gong,Hong-Qiang Fan

DOI: https://doi.org/10.1016/j.ijhydene.2021.12.229

IF: 7.2

2022-02-01

International Journal of Hydrogen Energy

Abstract:Dynamic potentials of polymer electrolyte membrane fuel cells (PEMFCs) lead to the corrosion of metal bipolar plates and significantly increase their interfacial contact resistance (ICR). Herein, two nano-thin C/Ti coatings with different thicknesses are prepared on SS316L (C/Ti/SS) and examined under three types of polarization potential modes. The C100Ti60 coating has improved corrosion resistance than C20Ti140 coating. The C100Ti60 coating exhibits a low ICR of 2.67 mΩ cm2 and a small corrosion rate of 1.47 μA/cm2, highlighting the high electrical conductivity and corrosion resistance. Moreover, C100Ti60/SS achieves a slight degradation of ICR after polarization at 0.67 V and cyclic polarization between 0.43 and 0.73 V. However, the high potential of 1.43 V induces severe delamination of C layer, resulting in a remarkable increase of ICR. Analysis suggests that the Ti layer improves the oxidation resistance and the C layer could provide effective protection when the potential is below 1.13 V.

energy & fuels,electrochemistry,chemistry, physical