Research on the corrosion protection of in-situ prepared Li Al layered double hydroxides on AZ31 Mg alloy under standard atmospheric pressure and low temperature

Liyan Wang,Keqi Huang,Zi Yang,Rudolph Buchheit,Zhiyuan Feng

DOI: https://doi.org/10.1016/j.clay.2024.107585

IF: 5.907

2024-10-05

Applied Clay Science

Abstract:This work successfully prepared LiAl LDHs coatings on AZ31 Mg alloy under standard atmospheric pressure and low temperature. The whole process did not require a hydrothermal autoclave reactor and high pressure. Electrochemical test results showed that the coating was able to provide good corrosion protection performance. The LiAl LDHs coatings provided a large low-frequency impedance on AZ31. When the treatment time was 24 h, the maximum |Z| 0.01Hz at pH = 12 was 5.14 × 10 4 Ω∙cm 2 , which is more than an order of magnitude higher than the |Z| 0.01Hz of 1.81 × 10 3 Ω∙cm 2 for the bare sample. Under the same treatment conditions, the potentiodynamic polarization test results showed that the LiAl LDHs coated samples had a lower corrosion current density and a higher breakdown potential. The i corr was 1.78 × 10 −7 A/cm 2 and E br was −0.82 V SCE compared to the Mg substrate ( i corr of 1.13 × 10 −5 A/cm 2 and E br of −1.53 V SCE ). Additionally, LiAl LDHs coatings also had a significant inhibitory effect on cathodic hydrogen evolution, providing targeted protection to the cathodic areas.

mineralogy,chemistry, physical,materials science, multidisciplinary