Abstract:The present study employs X-ray photoelectron spectroscopy (XPS) to analyze plastic samples subjected to degradation processes with the aim to gain insight on the relevant chemical processes and disclose fragmentation mechanisms. Two model plastics, namely polystyrene (PS) and polyethylene (PE), are selected and analyzed before and after artificial UV radiation-triggered weathering, under simulated environmental hydrodynamic conditions, in fresh and marine water for different time intervals. The object of the study is to identify and quantify chemical groups possibly evidencing the occurrence of hydrolysis and oxidation reactions, which are the basis of degradation processes in the environment, determining macroplastic fragmentation. Artificially weathered plastic samples are analyzed also by Raman and FT-IR spectroscopy. Changes in surface chemistry with weathering are revealed by XPS, involving the increase in chemical moieties (hydroxyl, carbonyl, and carboxyl functionalities) which can be correlated with the degradation processes responsible for macroplastic fragmentation. On the other hand, the absence of significant modifications upon plastics weathering evidenced by Raman and FT-IR spectroscopy confirms the importance of investigating plastics surface, which represents the very first part of the materials exposed to degradation agents, thus revealing the power of XPS studies for this purpose. The XPS data on experimentally weathered particles are compared with ones obtained on microplastics collected from real marine environment for investigating the occurring degradation processes.

What problem does this paper attempt to address?

This paper attempts to explore the chemical changes during the degradation process of plastics in the marine environment through X - ray photoelectron spectroscopy (XPS) studies, in order to reveal the chemical mechanisms leading to the fragmentation of macroscopic plastics. Specifically, the study selected two model plastics - polystyrene (PS) and polyethylene (PE), and through aging experiments triggered by artificial ultraviolet radiation, treated these plastic samples at different time intervals in fresh water and seawater respectively under simulated environmental hydrodynamic conditions. The main purpose of the study was to identify and quantify the chemical groups that may indicate the occurrence of hydrolysis and oxidation reactions, which are the basis for the degradation of plastics in the environment and ultimately lead to the fragmentation of macroscopic plastics. ### Research Background - **Plastic Pollution Problem**: Since the large - scale production began in the late 1940s, about 8 billion tons of plastics have been produced globally, and about 6 billion tons have been discarded. Due to poor management, these plastics enter the natural environment, especially in the ocean, where plastics will undergo processes such as physical erosion, hydrolysis, oxidation and photodegradation, gradually decomposing from macroscopic plastics (> 5 mm) into microplastics (< 5 mm) and nanoplastics (1 nm - 1 μm). - **Degradation Mechanisms**: The degradation of plastics is mainly driven by hydrolysis and oxidation/photo - oxidation processes. Ultraviolet (UV) radiation, especially the UV - B (280 - 315 nm) part, has enough energy to initiate the breakage of polymer chains, thus starting the degradation process. ### Research Methods - **Experimental Design**: The study adopted XPS technology to analyze the changes in surface chemistry of polystyrene (PS) and polyethylene (PE) during the aging process triggered by artificial ultraviolet radiation. The experimental conditions included different time intervals and fresh water and seawater environments. - **Control Experiment**: In order to distinguish the effects of ultraviolet radiation and other factors, the study also carried out control experiments in dark conditions. ### Main Findings - **Surface Chemical Changes**: XPS analysis showed that the oxygen content on the surface of artificially aged plastic samples increased significantly, especially the formation of functional groups such as hydroxyl, carbonyl and carboxyl groups. The increase in these functional groups is closely related to the hydrolysis and oxidation reactions during the plastic degradation process. - **The Role of Ultraviolet Radiation**: Compared with the samples treated in the dark, the oxygen content on the surface of plastics irradiated by ultraviolet radiation was significantly higher, indicating that ultraviolet radiation plays a key role in promoting the formation of oxygen - containing species. - **The Influence of Seawater**: Compared with the samples treated in fresh water, the plastic samples treated in seawater had similar surface chemical changes, but the salt adsorption in seawater may partially weaken the ultraviolet exposure, thus slightly slowing down the degradation process. ### Conclusions - **Application of XPS Technology**: XPS technology can provide detailed information on the chemical changes on the plastic surface, which is helpful for understanding the degradation mechanism of plastics in the marine environment. - **Practical Applications**: The research results not only help to understand the degradation process of plastics in the natural environment, but also can provide a scientific basis for formulating strategies to reduce plastic pollution. In general, this paper deeply explored the degradation process of plastics in the marine environment through XPS technology, revealed the important roles of ultraviolet radiation and hydrolysis in plastic degradation, and provided important reference data for future research.

Insights into Plastic Degradation Processes in Marine Environment by X-ray Photoelectron Spectroscopy Study

Multi-Analytical Approach to Characterize the Degradation of Different Types of Microplastics: Identification and Quantification of Released Organic Compounds

Physicochemical alterations on UV aged polymers leading to microplastics formation: A multi-tiered study of polyester, polycarbonate and polyamide

Laboratory-Simulated Photoirradiation Reveals Strong Resistance of Primary Macroplastics to Weathering

Physio-chemical degradation of single-use plastics in natural weather and marine environments

An advanced analytical approach to assess the long-term degradation of microplastics in the marine environment

An investigation into the stability and degradation of plastics in aquatic environments using a large-scale field-deployment study

3D imaging photocatalytically degraded micro- and nanoplastics

Fourier Transform Infrared Spectroscopy to Assess the Degree of Alteration of Artificially Aged and Environmentally Weathered Microplastics

Abiotic degradation and accelerated ageing of microplastics from biodegradable and recycled materials in artificial seawater

A Systematic Study on the Degradation Products Generated from Artificially Aged Microplastics

Exploring polystyrene weathering behavior: From surface traits to micro(nano)plastics and additives release

Cracking and Photo-Oxidation of Polyoxymethylene Degraded in Terrestrial and Simulated Marine Environments

Environmental Markers of Plastics and Microplastics

Abiotic weathering of plastic: Experimental contributions towards understanding the formation of microplastics and other plastic related particulate pollutants

Revealing the long-term impact of photodegradation and fragmentation on HDPE in the marine environment: Origins of microplastics and dissolved organics

Early signs of plastic degradation and fragmentation: A 40-day study in marine environments

Erosion of rigid plastics in turbid (sandy) water: quantitative assessment for marine environments and formation of microplastics

From Macro to Micro Plastics; Influence of Photo-oxidative Degradation

Degradation assessment of high-density polyethylene (HDPE) debris after long exposure to marine conditions