Abstract:Mineralized materials are gaining increased interest recently in a number of fields, especially in bone tissue engineering as bone replacement materials as well as in the architecture-built environment as structural building materials. Until the moment, there has not been a unified sustainable approach that addresses this multi-scale application objective by developing a self-mineralized material with minimum consumption of materials and processes. Thus, in the current study, a hydrogel developed from sodium alginate, gelatine, and calcium phosphate dibasic (CPDB) was optimized in terms of rheological properties and mineralization capacity through the formation of hydroxyapatite crystals. The hydrogel composition process adopted a three-stage, thermally induced chemical cross-linking to achieve a stable and enhanced hydrogel. The 6% CPDB-modified SA–gelatine hydrogel achieved the best rheological properties in terms of elasticity and hardness. Different concentrations of epigallocatechin gallate were tested as well as a rheological enhancer to optimize the hydrogel and to boost its anti-microbial properties. However, the results from the addition of EPGCG were not considered significant; thus, the 6% CPDB-modified SA–gelatine hydrogel was further tested for mineralization by incubation in various media, without and with cells, for 7 and 14 days, respectively, using scanning electron microscopy. The results revealed significantly enhanced mineralization of the hydrogel by forming hydroxyapatite platelets of the air-incubated hydrogel (without cells) in non-sterile conditions, exhibiting antimicrobial properties as well. Similarly, the air-incubated bioink with osteosarcoma SaOs-2 cells exhibited dense mineralized topology with hydroxyapatite crystals in the form of faceted spheres. Finally, the FBS-incubated hydrogel and FBS-incubated bioink, incubated for 7 and 14 days, respectively, exhibited less densely mineralized topology and less distribution of the hydroxyapatite crystals. The degradation rate of the hydrogel and bioink incubated in FBS after 14 days was determined by the increase in dimensions of the 3D-printed samples, which was between 5 to 20%, with increase in the bioink samples dimensions in comparison to their dimensions post cross-linking. Meanwhile, after 14 days, the hydrogel and bioink samples incubated in air exhibited shrinkage: a 2% decrease in the dimensions of the 3D-printed samples in comparison to their dimensions post cross-linking. The results prove the capacity of the developed hydrogel in achieving mineralized material with anti-microbial properties and a slow-to-moderate degradation rate for application in bone tissue engineering as well as in the built environment as a structural material using a sustainable approach.

Sustainable Development of a Bioactive Material from Recycled Rice Husk and Eggshell for Bone Regeneration Application

In vitro study of the biphasic calcium phosphate/chitosan hybrid biomaterial scaffold fabricated via solvent casting and evaporation technique for bone regeneration

3D Printed High-Strength Bioceramic Dome Scaffolds with Controllable Biodegradation for Guided Bone Regeneration

Porous calcium silicate bioactive material-alginate composite for bone regeneration

Bioactive material‑sodium alginate-polyvinyl alcohol composite film scaffold for bone tissue engineering application

Silk Fibroin 3D Microparticle Scaffolds with Bioactive Ceramics: Chemical, Mechanical, and Osteoregenerative Characteristics

Composition control in biphasic silicate microspheres on stimulating new bone regeneration and repair of osteoporotic femoral bone defect

Engineering Scaffolds Integrated with Calcium Sulfate and Oyster Shell for Enhanced Bone Tissue Regeneration

Effect of Bone Morphogenic Protein-2-Loaded Mesoporous Strontium Substitution Calcium Silicate/Recycled Fish Gelatin 3D Cell-Laden Scaffold for Bone Tissue Engineering

Preparation of Eggshell Derived HA-BT Composite for Biomedical Applications

Biomimetic Approach for Enhanced Mechanical Properties and Stability of Self-Mineralized Calcium Phosphate Dibasic–Sodium Alginate–Gelatine Hydrogel as Bone Replacement and Structural Building Material

Preparation and Characterization of Demineralised Bone Matrix from Fish Waste

Facile synthesis of in situ bismuth-doped calcium phosphate nanocomposite integrated injectable biopolymer hydrogel slurry for bone regeneration

Innovative Marine‐Sourced Hydroxyapatite, Chitosan, Collagen, and Gelatin for Eco‐Friendly Bone and Cartilage Regeneration

Transforming Natural Eggshell and Diatomite into Bioactive Calcium Silicate Material for Bone Regeneration

Biomimetic Fabrication of Sr-Silk Fibroin Co-Assembly Hydroxyapatite Based Microspheres with Angiogenic and Osteogenic Properties for Bone Tissue Engineering

Investigation on the Porous Biomaterial for Bone Reconstruction with Addition of Bio-Mimetic Nano-Sized Inorganic Particles

Green Synthesized Magnesium Oxide Nanoparticles Reinforce Osteogenesis Properties of Bacterial Cellulose Scaffolds for Bone Tissue Engineering Applications: An In Vitro Assessment

Optimization of Biologically Inspired Electrospun Scaffold for Effective Use in Bone Regenerative Applications

In‐situ Enzymatic Reaction Generates Magnesium‐Based Mineralized Microspheres with Superior Bioactivity for Enhanced Bone Regeneration

A Novel Photocrosslinked Phosphate Functionalized Chitosan-Sr5(PO4)2SiO4 Composite Hydrogels and in Vitro Biomineralization, Osteogenesis, Angiogenesis for Bone Regeneration Application