Large-Scale and Highly Efficient Production of Ultrafine PVA Fibers by Electro-Centrifugal Spinning for NH3 Adsorption

Youye Ma,Kanghui Cai,Guojie Xu,Yueling Xie,Peng Huang,Jun Zeng,Ziming Zhu,Jie Luo,Huawen Hu,Kai Zhao,Min Chen,Kun Zheng
DOI: https://doi.org/10.3390/ma16072903
IF: 3.4
2023-04-07
Materials
Abstract:Ultrafine Polyvinyl alcohol (PVA) fibers have an outstanding potential in various applications, especially in absorbing fields. In this manuscript, an electrostatic-field-assisted centrifugal spinning system was designed to improve the production efficiency of ultrafine PVA fibers from PVA aqueous solution for NH3 adsorption. It was established that the fiber production efficiency using this self-designed system could be about 1000 times higher over traditional electrospinning system. The produced PVA fibers establish high morphology homogeneity. The impact of processing variables of the constructed spinning system including rotation speed, needle size, liquid feeding rate, and voltage on fiber morphology and diameter was systematically investigated by SEM studies. To acquire homogeneous ultrafine PVA fiber membranes, the orthogonal experiment was also conducted to optimize the spinning process parameters. The impact weight of different studied parameters on the spinning performance was thus provided. The experimental results showed that the morphology of micro/nano-fibers can be well controlled by adjusting the spinning process parameters. Ultrafine PVA fibers with the diameter of 2.55 μm were successfully obtained applying the parameters, including rotation speed (6500 rpm), needle size (0.51 mm), feeding rate (3000 mL h−1), and voltage (20 kV). Furthermore, the obtained ultrafine PVA fiber mat was demonstrated to be capable of selectively adsorbing NH3 gas relative to CO2, thus making it promising for NH3 storage and other environmental purification applications.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is: **How to produce ultrafine polyvinyl alcohol (PVA) fibers on a large scale and efficiently by Electro - Centrifugal Spinning (ECS) technology, and improve their performance in ammonia (NH₃) adsorption**. Specifically, the paper focuses on the following aspects: 1. **Improving production efficiency**: Although the traditional electrospinning (ES) method can produce nanofibers with excellent morphology, its production efficiency is low, and the solution supply rate is only about 1 mL/h. In addition, ES requires a high voltage, which is costly and has safety risks. Although centrifugal spinning (CS) has high production efficiency, the morphology and distribution uniformity of the fibers are not as good as those of ES. Therefore, the paper proposes to combine the advantages of ES and CS and use ECS technology to significantly improve the production efficiency of PVA fibers. 2. **Optimizing fiber morphology and diameter distribution**: The paper systematically studied the effects of parameters such as rotation speed, needle size, liquid supply rate, and voltage on fiber morphology and diameter, and optimized the spinning process parameters by orthogonal experimental design, and finally obtained uniform ultrafine PVA fibers. Research shows that adjusting these parameters can effectively control the morphology and diameter of the fibers. 3. **Improving NH₃ adsorption performance**: The paper also explored the performance of the prepared PVA fibers in NH₃ adsorption, and found that they have a higher selective adsorption capacity relative to CO₂. This makes PVA fibers show great potential in NH₃ storage and other environmental purification applications. ### Key conclusions - Through ECS technology, the fiber production efficiency is increased by about 1000 times compared with the traditional ES. - The fiber morphology is uniform, the diameter is controllable, and the fiber diameter is 2.55 μm under the best conditions (rotation speed 6500 rpm, needle size 0.51 mm, liquid supply rate 3000 mL/h, voltage 20 kV). - PVA fibers have a highly selective adsorption performance for NH₃, which is better than that for CO₂, and are suitable for fields such as NH₃ storage and environmental purification. ### Formula summary - **Centrifugal force formula**: \[ F_c = m\cdot r\cdot\omega^2 \] where \(F_c\) is the centrifugal force, \(m\) is the mass, \(r\) is the rotation radius, and \(\omega\) is the angular velocity. - **Electric field force formula**: \[ F_e = q\cdot E \] where \(F_e\) is the electric field force, \(q\) is the charge amount, and \(E\) is the electric field intensity. Through these improvements, the paper shows the significant advantages of ECS technology in efficiently producing ultrafine PVA fibers and enhancing their functional performance.