Abstract:In this study, a natural zeolite supported Co-B catalyst (Co-B/Zeolite) with a Co content of 10 wt.% was prepared by impregnation and chemical reduction method to release hydrogen gas from an alkaline sodium borohydride (NaBH 4 ) solution. The synthesized catalyst was characterized with various characterization techniques, including X-ray diffraction (XRD), X-ray fluorescence (XRF), inductively coupled plasma mass spectroscopy (ICP-MS), Brunauer–Emmett–Teller (BET), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), Fourier transform infrared (FTIR), and X-ray photoelectron spectroscopy (XPS), etc. It was found that the BET specific surface area of Co-B/Zeolite (26.03 m 2 g −1 ) was roughly double that of the zeolite (13.12 m 2 g −1 ). The Co ratio in the catalyst was found to be 12.02 wt.% by EDX analysis. ICP-MS examination of the catalyst revealed a B/Co atomic ratio of 0.64. No peaks associated with Co-B were observed in the XRD pattern of the catalyst, indicating the amorphous nature of the component. Parameters that have significant effects on the hydrolysis reaction, such as catalyst amount, sodium hydroxide and sodium borohydride concentrations, and reaction temperature, were investigated. The hydrogen generation rate (HGR) was found to be 1732 mL min −1 g cat −1 in the presence of 100 mg of Co-B/Zeolite in 5 wt.% NaOH and 5 wt.% NaBH 4 solution at 50 °C. The experimental results were well fitted to the zero-order kinetic model ( k 0 = 0.0296–0.1619 mol min −1 g cat −1 for 20–50 °C). The activation energy ( E a ) of the catalytic reaction was found to be 44.98 kJ mol −1 . Meanwhile, the reusability evaluations showed that the catalyst preserves high stability and can still sustain 73% of its initial activity after 5 catalytic cycles.

Hydrogen generation from sodium borohydride hydrolysis using a heterogeneous biocatalyst prepared with Zabrus tenebrionides Goeze 1777 (Coleoptera: Carabidae) chitin

Efficient Hydrogen Generation From The Nabh4 Hydrolysis By Cobalt-Based Catalysts: Positive Roles Of Sulfur-Containing Salts

A highly active Co-B catalyst for hydrogen generation from sodium borohydride hydrolysis

Efficient and Stable Co-B Catalyst Supported on Natural Zeolite for Hydrogen Generation from Hydrolysis of Alkaline NaBH4 Solution

Ultrafine cobalt nanoparticles supported on carbon nanospheres for hydrolysis of sodium borohydride

Graphene-Modified Co-B-P Catalysts for Hydrogen Generation from Sodium Borohydride Hydrolysis

Catalytic Hydrogen Evolution of NaBH4 Hydrolysis by Cobalt Nanoparticles Supported on Bagasse-Derived Porous Carbon

Carbon nanospheres supported bimetallic Pt-Co as an efficient catalyst for NaBH4 hydrolysis

Hydrogen Production from NaBH4 in a Mixed Water–Ethanol Solution Catalyzed by Co-W-Mo-B Catalyst

Hydrolysis of NaBH4 using carbonized melamine foam-supported cobalt borate composite catalyst for H2 production

Hydrogen Generation from Sodium Borohydride Hydrolysis Accelerated by Zinc Chloride Without Catalyst: A Kinetic Study

High-Surface-Area Co-Cu-B Monolithic Self-Supported Catalyst for Efficient Sodium Borohydride Hydrolysis

Kinetically promoted hydrogen generation by Ru nanoparticles decorated CoB2O4 on mesoporous carbon spheres with rich oxygen vacancies for NaBH4 hydrolysis

Optimizing Hydrogen Production with a Zinc Ferrocyanide–Carbon Nanotube Catalyst

Preparation of Co–P–B/foam Ni catalyst and its catalytic performance for hydrogen production by hydrolysis of NaBH4 solution

Synthesis of “needle-cluster” NiCo2O4 carbon nanofibers and loading of Co-B nanoparticles for hydrogen production through the hydrolysis of NaBH4

Hierarchical porous cobalt nanoparticles encapsulated in heteroatom-doped hollow carbon as an enhancing multifunctional catalyst for hydrolysis of sodium borohydride and hydrogenation of bromate in water

Bacterial cellulose derived carbon as a support for catalytically active Co–B alloy for hydrolysis of sodium borohydride

Highly Active and Robust Catalyst: Co2B-Fe2B Heterostructural Nanosheets with Abundant Defects for Hydrogen Production

Electrosynthesis of Ni-Co/Hydroxyapatite as a Catalyst for Hydrogen Generation via the Hydrolysis of Aqueous Sodium Borohydride (NaBH4) Solutions

Solid-State NaBH4 Composites as Hydrogen Generation Material: Effect of Thermal Treatment of a Catalyst Precursor on the Hydrogen Generation Rate