Abstract:Most semiconductors exhibit a saturation of free carriers when heavily doped with extrinsic dopants. This carrier saturation or “doping limit” is known to be related to the formation of native compensating defects, which, in turn, depends on the energy positions of their conduction band minimum and valence band maximum. Here, we carried out a systematic study on the n-type doping limit of GaAs via ion implantation and showed that this doping limitation can be alleviated by the transient process of pulsed laser melting (PLM). For n-type doping, both group VI (S) and amphoteric group IV (Si and Ge) dopants were implanted in GaAs. For comparison, p-type doping was also studied using Zn as the acceptor. Implanted dopants were activated by the PLM method, and the results are compared to rapid thermal annealing (RTA). Our results reveal that for all n-type dopants, while implantation followed by the RTA results in a similar saturation electron concentration of 2–3 × 1018 cm−3, the transient PLM process is capable of trapping high concentration of dopants in the substitutional site, giving rise to a carrier concentration of >1019 cm−3, exceeding the doping limit of GaAs. However, due to scatterings from point defects generated during PLM, the mobility of n-type GaAs after PLM is low (∼80–260 cm2/V s). Subsequent RTA after PLM (PLM + RTA) is able to remove these point defects and recover the mobility to ∼1000–2000 cm2/V s. The carrier concentrations of these PLM + RTA samples are reduced but are still a factor of 3 higher than RTA only GaAs. This can be understood as the dopants are already incorporated in the substitutional site after PLM; they are less likely to be “deactivated” by subsequent RTA. This work is significant to the understanding of doping mechanisms in semiconductors and provides a means for device applications, which require materials with ultra-high doping.

Modulation doping of GaAs/AlGaAs core-shell nanowires with effective defect passivation and high electron mobility

A Roadmap for Controlled and Efficient n-type Doping of Self-assisted GaAs Nanowires Grown by Molecular Beam Epitaxy

Band structure of n- and p-doped core-shell nanowires

Significant Resistance Reduction in Modulation‐Doped Silicon Nanowires via Aluminum‐Induced Acceptor States in SiO2

Doubling the mobility of InAs/InGaAs selective area grown nanowires

Towards low-dimensional hole systems in Be-doped GaAs nanowires

P-Type Dopant Incorporation and Surface Charge Properties of Catalyst-Free Gan Nanowires Revealed by Micro-Raman Scattering and X-Ray Photoelectron Spectroscopy

Overcoming the doping limit in GaAs by ion implantation and pulsed laser melting

Electrical properties of highly-doped MBE-grown gallium phosphide nanowires

Near-thermal limit gating in heavily-doped III-V semiconductor nanowires using polymer electrolytes

Sub-nanometer ultrathin epitaxy of AlGaN and its application in efficient doping

A study of n-doping in self-catalyzed GaAsSb nanowires using GaTe dopant source and ensemble nanowire near-infrared photodetector

Studies on Carrier Recombination in GaN/AlN Quantum Dots in Nanowires with a Core–Shell Structure

Photocurrent and Photoconductance Properties of a GaAs Nanowire

Doping Dependent Crystal Structures and Optoelectronic Properties of N-Type Cdse:Ga Nanowries

InAs/InP radial nanowire heterostructures as high electron mobility devices.

Tunable Transport Properties of Dual-Gated InAs/GaSb Core/shell Nanowires

Monolithic lateral p-n junction GaAs nanowire diodes via selective lateral epitaxy

Single photon emitters in thin GaAsN nanowire tubes grown on Si

Different Doping Behaviors of Silicon in Zinc Blende and Wurtzite GaAs Nanowires: Implications for Crystal-Phase Device Design

Optimization of p-i-n GaAs/AlGaAs Heterojunction Nanowire Solar Cell for improved Optical and Electrical Properties