Abstract:The x%Ni/Sm2O3-MnO (x = 0, 10, 15, 20) catalysts derived from SmMn2O5 mullite were prepared by solution combustion and impregnation method; auto-thermal reforming (ATR) of acetic acid (HAc) for hydrogen production was used to explore the metal-support effect induced by Ni loadings on the catalytic reforming activity and product distribution. The 15%Ni/Sm2O3-MnO catalyst exhibited optimal catalytic performance, which can be due to the appropriate Ni loading inducing a strong metal–support interaction to form a stable Ni/Sm2O3-MnO active center, while side reactions, such as methanation and ketonization, were well suppressed. According to characterizations, Sm2O3-MnO mixed oxides derived from SmMn2O5 mullite were formed with oxygen vacancies; nevertheless, loading of Ni metal further promoted the formation of oxygen vacancies, thus enhancing adsorption and activation of oxygen-containing intermediate species and resulting in higher reactivity with HAc conversion near 100% and hydrogen yield at 2.62 mol-H2/mol-HAc.

What problem does this paper attempt to address?

### Problems Addressed by the Paper The paper primarily explores the catalytic performance of nickel-based catalysts with different contents on samarium manganese oxide (composite oxide derived from SmMn2O5) in the process of hydrogen production from acetic acid via Auto-Thermal Reforming (ATR). 1. **Research Background**: - With the increasing consumption of fossil fuels, there is an urgent need to explore sustainable energy alternatives to meet the growing energy demand. - Hydrogen, as a green energy carrier with high energy density (122 kJ/g), has attracted widespread attention. - The current main hydrogen production technology is through the thermochemical conversion of fossil resources, but this method inevitably produces carbon emissions. - Biomass and its derivatives as raw materials for hydrogen production meet the requirements of energy renewability and carbon neutrality. 2. **Specific Issues**: - The catalytic activity and product distribution of Ni/Sm2O3-MnO catalysts with different nickel loadings (0%, 10%, 15%, 20%) in the auto-thermal reforming of acetic acid were investigated. - The effect of Ni loading on catalytic activity was studied, and the reasons for the optimal Ni loading (15%) were explored. - The stability of the catalyst during the reaction and the inhibition of side reactions (such as methanation and ketonization) were studied. 3. **Experimental Design and Results**: - Catalysts with different Ni loadings were prepared by solution combustion and impregnation methods. - The performance of these catalysts in the auto-thermal reforming of acetic acid at 700°C was tested in a fixed-bed reactor. - The results showed that the 15% Ni/Sm2O3-MnO catalyst exhibited the best catalytic performance, which may be due to the appropriate Ni loading promoting strong metal-support interactions, forming stable active centers. Through these studies, the paper aims to optimize the catalyst performance in the auto-thermal reforming of acetic acid for hydrogen production, increase hydrogen yield, and reduce the generation of by-products.

Mullite-like SmMn2O5-Derived Composite Oxide-Supported Ni-Based Catalysts for Hydrogen Production by Auto-Thermal Reforming of Acetic Acid

Acid-Resistant Performance of Ni-Based Hydrogenation Catalysts Supported by Hydrophobic Activated Carbon

Durable Mn(II)Cr(III)Ox composites-supported Ni-based catalysts with wide dynamic range for hydrogen production via auto-thermal reforming of acetic acid

Effective Hydrogen Production from Partial Oxidation of Propane over Composite Ni/Al2O3-SiC Catalyst

Mn-doped NiTiO3 catalysts for hydrogen production via auto-thermal reforming of acetic acid

Reaction Induced Ni/MgTi2O5 Interface Promotes the Resistance to Sintering and Oxidation in Auto-Thermal Reforming of Acetic Acid

Additive WO2 promotes Ni - based catalyst for hydrogen production from auto-thermal reforming of acetic acid

Solid solution-type Sm-Pr-O supported nickel-based catalysts for auto-thermal reforming of acetic acid: Role of Pr in solid solution

Au-NiO/TiO_2 Catalyst for Methanol Autothermal Reforming to Produce Hydrogen

Atomically Dispersed Ni/-MoC Catalyst for Hydrogen Production from Methanol/Water

Hydrogen production by aqueous phase reforming of methanol over stable C-modified NiMgAl hydrotalcite catalyst

Atomically Dispersed Ni/α-MoC Catalyst for Hydrogen Production from Methanol/Water

A Highly Active NiMoAl Catalyst Prepared by a Solvothermal Method for the Hydrogenation of Methyl Acrylate

Synthesis of Ni-Co Catalysts Supported on Flower-like MgAl Composite Oxide for Hydrogen Production by <i>n</i>-Dodecane Steam Reforming

Ce1-xSrxO2-δ solid solution support cobalt-based catalysts for hydrogen production via auto-thermal reforming of acetic acid

Promoted Multimetal Oxide Catalysts for the Generation of Hydrogen Via Ammonia Decomposition

Ni-based bimetallic catalysts for hydrogen production via (sorption-enhanced) steam methane reforming

Sol–gel synthesis of Ni and Ni supported catalysts for hydrogen production by methane decomposition

A Comparative Research on the Catalytic Activity of La2O3 and Γ-Al2o3 Supported Catalysts for Acetic Acid Steam Reforming

Cost-Effective Single-Step Synthesis of Metal Oxide-Supported Ni Catalyst for H2-Production Through Dry Reforming of Methane

Hydrogen production from acetic acid steam reforming over Ti-modified Ni/Attapulgite catalysts