Abstract:We present a systematic study of the properties of TiN films by varying the deposition conditions in an ultra-high-vacuum reactive magnetron sputtering chamber. By increasing the deposition pressure from 2 to 9 mTorr while keeping a nearly stoichiometric composition of Ti(1-x)N(x) (x=0.5), the film resistivity increases, the dominant crystal orientation changes from (100) to (111), grain boundaries become clearer, and the strong compressive strain changes to weak tensile strain. The TiN films absorb a high concentration of contaminants including hydrogen, carbon, and oxygen when they are exposed to air after deposition. With the target-substrate distance set to 88 mm the contaminant levels increase from ~0.1% to ~10% as the pressure is increased from 2 to 9 mTorr. The contaminant concentrations also correlate with in-plane distance from the center of the substrate and increase by roughly two orders of magnitude as the target-substrate distance is increased from 88 mm to 266 mm. These contaminants are found to strongly influence the properties of TiN films. For instance, the resistivity of stoichiometric films increases by around a factor of 5 as the oxygen content increases from 0.1% to 11%. These results suggest that the sputtered TiN particle energy is critical in determining the TiN film properties, and that it is important to control this energy to obtain high-quality TiN films. Superconducting coplanar waveguide resonators made from a series of nearly stoichiometric films grown at pressures from 2 mTorr to 7 mTorr show an increase in intrinsic quality factor from ~10^4 to ~10^6 as the magnitude of the compressive strain decreases from nearly 3800 MPa to approximately 150 MPa and the oxygen content increases from 0.1% to 8%. The films with a higher oxygen content exhibit lower loss, but the nonuniformity of the oxygen incorporation hinders the use of sputtered TiN in larger circuits.

High resistance of superconducting TiN thin films against environmental attacks

High resistance of superconducting TiN thin films against environmental attacks

Environmental Response Characteristics of Epitaxial Superconducting La0.8Sr0.2NiO2 Thin Films

Stability of Superconducting Nd0.8Sr0.2NiO2 Thin Films

Pressure Tuning of Superconductivity in TiN Thin Films

A New Technique to Achieve Thick Tl2Ba2CaCu2O8 Films for Advanced Applications

Pristine Titanium Carbide Mxene Films With Environmentally Stable Conductivity And Superior Mechanical Strength

Resilient Growth of Highly Crystalline Topological Insulator-Superconductor Heterostructure Enabled by Ex-situ Nitride Film

Wafer-Scale Epitaxy of Flexible Nitride Films with Superior Plasmonic and Superconducting Performance

Enhanced Superconductivity in TiO Epitaxial Thin Films

The microstructure and mechanical properties of Ti(CoCr)N films produced by DC magnetron sputtering

Atomic-Scale Preparation And Characterization Of High-Temperature Superconducting Thin Films

From weak to strong-coupling superconductivity tuned by substrate in TiN films

Sputtered TiN films for superconducting coplanar waveguide resonators

Electrical Stability and Degradation Mechanism of CrSi(Ni, Al) Resistive Films in Alkaline Aqueous Environments

Corrosion behavior of Ti2 AlN powders under hydrothermal conditions in acid solutions

Resilient Growth of a Highly Crystalline Topological Insulator-Superconductor Heterostructure Enabled by an Ex Situ Nitride Film

Plasma-enhanced atomic layer deposition of titanium nitride for superconducting devices

Unveiling the Degradation Mechanism of High-Temperature Superconductor Bi2Sr2CaCu2O8+δ in Water-Bearing Environments

Crystal orientation-dependent superconductivity in titanium nitride films