Tailoring wetting properties of organic hole-transport interlayers for slot-die coated perovskite solar modules

T.S. Le,I.A. Chuykoa,L.O. Luchnikova,K.A. Ilicheva,P.O. Sukhorukova,D.O. Balakirev,N.S. Saratovsky,A.O. Alekseev,S.S. Kozlov,D.S. Muratov,V.V. Voronov,P.A. Gostishchev,D. A. Kiselev,T.S. Ilina,A.A. Vasilev,A. Y. Polyakov,E.A. Svidchenko,O.A. Maloshitskaya,Yu. N. Luponosov,D.S. Saranin
2024-06-13
Abstract:The use of self-assembled monolayers (SAMs) with anchoring groups was considered as an effective approach for interface engineering in perovskite solar cells with metal oxide charge transporting layers. However, the coating of SAM layers in PSMs by means of a slot-die is a challenging process due to the low viscosity of the solutions and the low wettability of the films. In this study, we integrate a triphenylamine-based polymer, pTPA-TDP, blended with SAM based on 5-[4-[4-(diphenylamino) phenyl] thiophene-2-carboxylic acid (TPATC), to address the challenges of uniform slot-die coating and interface passivation in large-area modules. We fabricated p-i-n oriented PSMs on 50x50 mm2 substrates (12-sub-cells) with NiO hole transport layer (HTL) and organic interlayers for surface modification. Wetting angle mapping demonstrated that ununiform regions of the slot-die coated SAM have hydrophobicity with contact angle values up to 90°, causing fluctuations in absorber thickness and the presence of macro-defects at buried interfaces. The incorporation of the blended interlayer to NiO/perovskite junction homogenized the surface wettability (contact angle=40°) and mitigated lattice strain in the absorber. This enabled the effective use of SAM properties on a large-area surface, improving energy level alignment and enhancing the power conversion efficiency (PCE) of the modules from 13.98% to 15.83% and stability (ISOS-L-2, T80 period) from 500-1000 hours to 1630 hours. Investigation of PSMs upon cooling till -5 °C showed that the PCE increased by +0.19%/°C for samples with NiO HTL, while using SAM and blended interlayers raised the coefficient to ~0.40%/°C due to changes in activation energy and trap contributions to device performance across a wide temperature range.
Applied Physics,Materials Science
What problem does this paper attempt to address?
The paper primarily aims to address the challenges encountered in the large-scale manufacturing of Perovskite Solar Modules (PSMs), particularly the interfacial engineering challenges when using slot-die coating technology. Specifically, the research focuses on the following key points: 1. **Improving Wetting Properties**: By adjusting the wettability of Organic Hole-Transport Interlayers to enhance the uniformity and quality of large-area modules. 2. **Using Self-Assembled Monolayers (SAMs) Materials**: Mixing self-assembled monolayers based on 5-[4-[4-(diphenylamino)phenyl]thiophene-2-carboxylic acid] (TPATC) with triphenylamine-based polymer pTPA-TDP to address the issues of non-uniformity and defects in large-area PSMs manufactured using slot-die coating technology. 3. **Enhancing Efficiency and Stability**: Improving the power conversion efficiency (PCE) and long-term operational stability of PSMs by optimizing the aforementioned mixed layer. 4. **Addressing Coating Challenges**: Tackling the challenges posed by the low viscosity solution and low wettability of the SAM layer when using slot-die coating technology, particularly the issues of film non-uniformity, absorber layer thickness fluctuations, and macroscopic interfacial defects. 5. **Achieving Uniformity**: The application of the mixed layer results in more uniform surface wettability of large-area modules (contact angle around 40°), reducing lattice strain, improving energy level alignment, and ultimately enhancing the performance of PSMs. 6. **Scaling to Industrial Production**: The research aims to provide solutions for large-scale industrial production, particularly achieving high-throughput production while maintaining cost-effectiveness. In summary, the main objective of this paper is to improve the performance and stability of large-area perovskite solar modules manufactured using slot-die coating technology by enhancing the wettability of organic interlayers and optimizing the application of self-assembled monolayer materials.