Effects of degumming conditions on the structure of the regenerated silk fibroin and the properties of its film

Ruixue Sun,Junli Hu

2024-05-31

Abstract:The traditional degumming method using sodium carbonate solution severely damages the structure of silk fibroin and results in low molecular weight, which limits the properties and applications of silk materials. In this study, we report a modified degumming method and compared it with the traditional one. The results indicate that compared with the traditional degumming method, the modified degumming method produces silk fibroin with higher \b{eta}-sheet content (53.43% vs 46.68%), higher crystallinity (44.92% vs 42.72%), and more concentrated molecular weight (100 ~ 300 kDa vs 72 ~ 300 kDa), while allowing for the same full removal of sericin. Correspondingly, the film of the silk fibroin prepared with the modified degumming method exhibits higher \b{eta}-sheet content (35.22% vs 32.82%), higher crystallinity (26.96% vs 25.53%), and higher tensile strength (87.91 MPa vs 72.62 MPa). This work provides a degumming method superior to the traditional one and lays a foundation for the development of high-performance silk materials.

Biological Physics,Soft Condensed Matter

What problem does this paper attempt to address?

The problem that this paper attempts to address is the severe damage to the structure of silk fibroin caused by traditional degumming methods, which leads to a reduction in its molecular weight, thereby limiting the performance and applications of silk materials. Specifically, traditional degumming methods use sodium carbonate solution to treat silk at high temperatures, which, although it can completely remove sericin, severely damages the structure of silk fibroin. Therefore, the researchers proposed an improved degumming method aimed at reducing damage to silk fibroin and enhancing the performance of silk materials.

By comparing traditional degumming methods with the improved degumming method, the researchers found that the improved method could retain higher β-sheet content, crystallinity, and a more concentrated molecular weight distribution while maintaining the complete removal of sericin. Correspondingly, silk fibroin films prepared using the improved degumming method exhibited higher β-sheet content, crystallinity, and tensile strength. These results indicate that the improved degumming method is superior to traditional methods and lays the foundation for the development of high-performance silk materials.