Size dependent photoemission study by electrochemical coarsening of nanoporous gold

Fatemeh Ebrahimi,Xinyan Wu,Maurice Pfeiffer,Hagen Renner,Nadiia Mameka,Manfred Eich,Alexander Petrov

2024-04-04

Abstract:The generation and utilization of hot charge carriers in plasmonic materials have emerged as a topic of significant importance, with profound implications across multiple disciplines, including optoelectronics, photovoltaics, photocatalysis, and sensing. In this study, we investigate the hot electron transfer from nanoporous gold (npAu) in dependence of the structure size, utilizing both the nanoscale feature size and the interconnected nature of this material. We employ photoelectron injection from nanoporous gold into the electrolyte under UV illumination as a test electron transfer process. Nanoporous gold thin films with sub-10 nm initial ligament diameter are stepwise coarsened by potential cycles in a photoelectrochemical setup, thereby allowing us to precisely probe the influence of ligament diameter on the photocurrent response. The resulting ligament diameter variations are confirmed by scanning electron microscopy (SEM) analysis. As the ligament diameter increased from 8 to 16 nm, there was a corresponding decrease in quantum efficiency proportional to the inverse ligament diameter squared. Such dependency is expected for electrons excited by surface collisions. For the small ligament diameter of 10 nm we estimate an emission efficiency of excited 6sp electrons as 3.14%, reaching 23% for the surface excited electrons.

Optics,Materials Science

What problem does this paper attempt to address?

The core problem that this paper attempts to solve is to explore the hot - electron transfer efficiency of nanoporous gold (npAu) at different structural sizes. Specifically, the researchers gradually change the nanoscale feature size of npAu through the electrochemical roughening method and precisely measure the influence of these changes on the photocurrent response through photo - emission experiments. The following are the main problems and goals of this research:

1. **Explore size - dependence**: The researchers aim to understand how the hot - electron emission efficiency in npAu changes with the structural size (especially the coordination diameter). They find that as the coordination diameter increases from 8 nm to 16 nm, the quantum efficiency shows an inverse relationship with the reciprocal of the square of the coordination diameter.

2. **Verify theoretical predictions**: The research results support the theoretical prediction that surface and geometric modifications significantly affect the plasma decay rate and the excitation of hot carriers. This relationship indicates that for coordination diameters less than 30 nm, surface photo - emission is dominant.

3. **Optimize photo - emission performance**: By controlling the electrochemical cycling conditions, the researchers can precisely regulate the roughening process of npAu, thereby achieving the optimization of photo - emission performance. This is of great significance for the development of high - efficiency optoelectronic devices, photovoltaic devices, photocatalysis, and sensing applications.

### Formula summary

- **Internal quantum efficiency formula**:
\[
\eta=\frac{N_{e}}{N_{ph}}=\frac{I_{ph}}{e\cdot A\cdot P}
\]
where \(\eta\) is the internal quantum efficiency, \(N_{e}\) is the number of emitted electrons, \(N_{ph}\) is the number of absorbed photons, \(I_{ph}\) is the photocurrent, \(e\) is the elementary charge, \(A\) is the absorptivity, and \(P\) is the incident light power.

- **Relationship between coordination diameter and quantum efficiency**:
\[
\eta = \frac{b}{L}+\frac{c}{L^{2}}
\]
where \(L\) is the coordination diameter, and \(b\) and \(c\) are fitting parameters.

### Experimental methods

To achieve the above goals, the researchers adopted the following methods:

- **Sample preparation**: Prepare npAu films with an initial coordination diameter less than 10 nm by the electrochemical dealloying method.

- **Electrochemical roughening**: Gradually increase the coordination diameter by performing cyclic voltammetry (CV) in sulfuric acid electrolyte.

- **Photo - emission measurement**: Evaluate the photo - emission efficiency at different coordination diameters by using photocurrent measurement under ultraviolet light irradiation.

- **Scanning electron microscope (SEM) characterization**: Confirm the change of the coordination diameter.

Through these methods, the researchers can systematically study the photo - emission characteristics of npAu and reveal its size - dependence law.