Rapid non-destructive inspection of sub-surface defects in 3D printed alumina through 30 layers with 7 μm depth resolution

C. Lapre,D. Brouczek,M. Schwentenwein,K. Neumann,N. Benson,C. R. Petersen,O. Bang,N. M. Israelsen

2024-03-27

Abstract:The use of additive manufacturing (AM) processes for industrial fabrication has grown rapidly over the last ten years. The most well-known AM technologies are fused deposition modelling and stereolithography techniques. One particular industry where 3D printing is advantageous over traditional fabrication techniques is within ceramic components due to its flexibility. To establish a new and improved level of print quality and reduce resource consumption in the 3D printing ceramics industry, there is a need for fast integrated, sub-surface and non-destructive inspection (NDI) with high resolution. Several techniques have already been developed for high-resolution NDI, such as X-ray computed tomography (XCT), but none of them are both fast, integrable, and non-destructive while allowing deep penetration with high resolution. In this study, we demonstrate sub-surface monitoring of 3D printed alumina parts to a depth of $\sim$0.7 mm in images of 400$\times$2048 pixels with a lateral resolution of 30$~\mu$m and depth (or axial) resolution of 7$~\mu$m . The results were achieved using mid-infrared optical coherence tomography (MIR OCT) based on a MIR supercontinuum laser with a 4$~\mu$m center wavelength. We find that it is possible to detect individual printed ceramic layers and track predefined defects through all four processing steps: green, preconditioned, debinded, and sintered. Our results also demonstrate how a defect in the green phase could affect the final product. Based on the understanding of how defects develop in maturing printed parts, we pave the way for NDI integration in AM, which can be combined with artificial intelligence and machine learning algorithms for automatic defect classification in volume production of a new standard of high quality ceramic components.

Optics

What problem does this paper attempt to address?

This paper mainly discusses the problem of fast and non-destructive detection of subsurface defects in 3D printed alumina components. With the widespread application of additive manufacturing (AM) technology in industrial production, especially for ceramic components, it is necessary to be able to quickly and high-resolution inspect the internal quality of 3D printed products to reduce resource waste. Currently available techniques such as X-ray computed tomography (XCT), although they have high resolution, are not suitable for fast, integrated, and deep-penetrating non-destructive testing.

The research team used a new method based on mid-infrared optical coherence tomography (MIR OCT) to achieve subsurface monitoring of 3D printed alumina components. A MIR supercontinuum laser with a central wavelength of 4 micrometers was used, realizing a depth of approximately 0.7 millimeters and an image resolution of 30 micrometers in the lateral direction and 7 micrometers in depth. Through this method, they were able to track the predetermined defects during the printing process, from the green stage to the sintering stage, revealing how the defects affect the final product.

In addition, the paper also discusses the influence of different printing materials and defect locations on the internal structure of the product, for example, top and bottom defects exhibit different effects in subsequent processing. The research results pave the way for the integration of non-destructive testing technology in AM, and in the future, it can be combined with artificial intelligence and machine learning algorithms to achieve automatic defect classification, thereby improving the mass production standards of high-quality ceramic components.

In summary, this paper aims to solve the problem of fast and high-precision non-destructive detection of internal defects in 3D printed ceramic components in order to improve printing quality and efficiency and reduce waste.