Abstract:A simple and rapid method is proposed for assessing the reduction in the lifetime of steel walls of the reactor vessel under neutron irradiation. The method is based on modeling the number of radiation defects by the behavior of a general time-dependent random process of death and birth and queuing theory. Necessary data for assessments: the estimated operating time of the reactor (in years), the actual operating time of the reactor, the accumulated fluence depending on time, the temperature on the walls of the reactor vessel, the neutron absorption cross section of the steel of the reactor walls, the energy of fast neutrons striking the walls. The main problem: getting this accurate data.

What problem does this paper attempt to address?

This paper mainly discusses the problem of lifetime assessment of nuclear reactor pressure vessel (RV) under neutron irradiation. The author proposes a simple and fast method to estimate the reduction of the RV steel wall's lifetime under neutron irradiation. The method is based on the birth-death model of stochastic processes and queueing theory to estimate the lifetime of the vessel wall. The study considers the radiation defects generated by the interaction between neutrons and the steel wall, and models the behavior of these defects using stochastic processes and describes the reactor's lifetime using queueing theory. The paper mentions that neutron irradiation leads to the degradation of material properties, especially the generation of vacancies and interstitial atoms in the lattice. The author describes this phenomenon using generating functions and mathematical models of birth-death processes, and applies queueing theory to analyze the effect of the reactor's operating time during irradiation on its lifetime. By calculating the dependence on different parameters such as neutron energy, absorption cross-section, and temperature, the paper shows the variation curve of the reactor's lifetime with operation time. The study also points out that the degree of embrittlement of the steel wall can be measured by the transition of the critical brittleness temperature, and this paper chooses the reduction of stable operating time as the measure. The paper analyzes the impact of different parameters (such as neutron energy, absorption cross-section, temperature, and cumulative neutron flux) on the reactor's lifetime through examples, and provides relevant curve graphs. The results show that these parameters have a significant impact on the reactor's lifetime. In conclusion, the paper attempts to address the problem of how to quickly assess the reduction of the service lifetime of nuclear reactor pressure vessels under neutron irradiation through simplified probability methods, and explores the key factors influencing this process.

Probabilistic assessment of the reactor vessel lifetime

Mechanical stability paradigm for prediction of rpv service life

Quick Evaluation Method for Defect Exceeding the Allowable Flaw Size in Pressure Vessel of Nuclear Reactor for Power Plant and Space Heating

The Unified Model for Irradiation Embrittlement Prediction of Reactor Pressure Vessel

Characterizing the flux effect on the irradiation embrittlement of reactor pressure vessel steels using machine learning

Analysis of Shift in Nil-Ductility Transition Reference Temperature for RPV Steels Due to Irradiation Embrittlement Using Probability Distributions and Gamma Process

On the history and status of reactor pressure vessel steel ductile to brittle transition temperature shift prediction models

Application of Flaw Updating Process on Probabilistic Integrity Analysis for a Reactor Pressure Vessel Subjected to Pressurized Thermal Shocks

Improvements to a probabilistic fracture mechanics code for evaluating the integrity of a RPV under transient loading

Sensitivity Study on the Effects of Nondestructive Examinations on Failure Probabilities of Reactor Pressure Vessels

Sensor degradation in nuclear reactor pressure vessels: the overlooked factor in remaining useful life prediction

Brittle Fracture Resistance of the Reflection Shield of a WWER-1000 Reactorunder Normal Operating and Emergency Conditions

Neural networks for prediction of swelling in austenitic steels irradiated by fast neutrons

A Statistical Model for Accessing Wall Thinning Rate Due to Flow Accelerated Corrosion Based on Inspection Data in Nuclear Power Plants

Application Of Flaw Updating Process On Probabilistic Structural Evaluation For A Reactor Pressure Vessel Under Pressurized Thermal Shocks

Creep behavior and life prediction of a reactor pressure vessel steel above phase‐transformation temperature via a deformation mechanism‐based creep model

Probabilistic fracture mechanics analyses of a reactor pressure vessel using the irradiation embrittlement evaluation based on the Bayesian nonparametric method

A Quasi Time-Domain Method for Fatigue Analysis of Reactor Pressure Vessels in Floating Nuclear Power Plants in Marine Environments

Simulation Study on Defect Damage Behavior of Fe under Irradiation Environment

A computational framework for probabilistic structural assessments of reactor components requiring complex code workflows

Mechanical characterization of synergistic thermal and irradiation effects on fracture resistance of stainless steel