Abstract:Colloidal quantum dots (cQDs) recently emerged as building blocks for semiconductor materials with tuneable properties. Electro-hydrodynamic printing can be used to obtain sub-micrometre patterns of cQDs without elaborate and aggressive photolithography steps. Post-deposition ligand exchange is necessary for the introduction of new functionalities into cQD solids. However, achieving a complete bulk exchange is challenging and conventional infrared spectroscopy lacks the required spatial resolution. Infrared nanospectroscopy (AFM-IR) enables quantitative analysis of the evolution of vibrational signals and structural topography on the nano-metre scale upon ligand substitution on lead sulphide (PbS) cQDs. A solution of ethane-dithiol in acetonitrile demonstrated rapid (~60 s) and controllable exchange of approximately 90% of the ligands, encompassing structures up to ~800 nm in thickness. Prolonged exposures (>1 h) led to the degradation of the microstructures, with a systematic removal of cQDs regulated by surface-to-bulk ratios and solvent interactions. This study establishes a method for the development of devices through a combination of tuneable photoactive materials, additive manufacturing of microstructures, and their quantitative nanometre-scale analysis.

What problem does this paper attempt to address?

This paper mainly discusses how to quantitatively analyze the ligand exchange process of colloidal quantum dots (cQDs) at the nanoscale. The study focuses on lead sulfide (PbS) quantum dots, which form sub-micron patterns using Electro-hydrodynamic printing (EHD) technology, avoiding complex lithography steps. Ligand exchange is crucial for introducing new functionalities into cQD solids, but achieving overall ligand exchange is challenging, and the spatial resolution of conventional infrared spectroscopy is insufficient. In the paper, researchers used Atomic Force Microscopy infrared spectroscopy (AFM-IR) technique to achieve quantitative analysis of ligand substitution on PbS quantum dots. The researchers first rapidly (approximately 60 seconds) and controllably exchanged approximately 90% of the ligands with ethane-dithiol (EDT) in acetonitrile. This influenced the structural thickness up to approximately 800 nanometers. However, prolonged exposure (over 1 hour) led to microstructural degradation, and the removal of quantum dots was controlled by the surface-to-volume ratio and solvent interactions. The study established a method combining tunable photoactive materials, additive manufacturing of microstructures, and nanoscale quantitative analysis for device development. The paper also compared two methods: Solid-state ligand exchange (SSLE) and Liquid-phase ligand exchange (LPLE), and pointed out that the high resolution of EHD printing made it possible to study the influence of ligand exchange on microstructures. Through AFM-IR, researchers found that the most effective ligand exchange was completed within just 60 seconds, regardless of thickness. Extending the processing time did not improve the removal of organic adsorbates but instead resulted in quantum dot loss and structural damage. In summary, this work developed a method for quantitatively studying ligand exchange at the nanoscale, which is important for the development of quantum dot-based microstructure functional devices.

AFM-IR of EHD-Printed PbS Quantum Dots: Quantifying Ligand Exchange at the Nanoscale

AFM-IR of Electrohydrodynamically Printed PbS Quantum Dots: Quantifying Ligand Exchange at the Nanoscale

Enhancing Quantum Dots for Bioimaging using Advanced Surface Chemistry and Advanced Optical Microscopy: Application to Silicon Quantum Dots (SiQDs)

The Role of Liquid Ink Transport in the Direct Placement of Quantum Dot Emitters Onto Sub-Micrometer Antennas by Dip-Pen Nanolithography.

Tailoring the Interfacial Structure of Colloidal "giant" Quantum Dots for Optoelectronic Applications.

Plasmon-Enhanced Surface-State Emission of CdSe Quantum Dots and Its Application to Microscale Luminescence Patterns

Optimizing the Infrared Photoelectric Detection Performance of Pbs Quantum Dots through Solid-State Ligand Exchange

Counterion-Mediated Ligand Exchange for PbS Colloidal Quantum Dot Superlattices.

Synergic Surface Modifications of PbS Quantum Dots by Sodium Acetate in Solid-State Ligand Exchange toward Short-Wave Infrared Photodetectors

Highly Stabilized Quantum Dot Ink for Efficient Infrared Light Absorbing Solar Cells

Controllable Electrolysis Reveals the Microscopic Composition of Lead Sulfide Quantum Dots

Colloidal Quantum Dot Inks for Single-Step-Fabricated Field-Effect Transistors: The Importance of Postdeposition Ligand Removal

Phase-Transfer Ligand Exchange of Lead Chalcogenide Quantum Dots for Direct Deposition of Thick, Highly Conductive Films

Electrohydrodynamic Printing‐Based Heterointegration of Quantum Dots on Suspended Nanophotonic Cavities

Ligand-Surface Interactions and Surface Oxidation of Colloidal PbSe Quantum Dots Revealed by Thin-film Positron Annihilation Methods

Formation of Colloidal In(As,P) Quantum Dots Active in the Short-Wave Infrared, Promoting Growth through Temperature Ramps

PbS Colloidal Quantum Dots: Ligand Exchange in Solution

The micropatterning of layers of colloidal quantum dots with inorganic ligands using selective wet etching

Quantum Dot Size Dependence on Ligand Exchange Driving Forces and Insights into the Structure of the Solvated Ligand Shell

Surface-Reconstructed InAs Colloidal Nanorod Quantum Dots for Efficient Deep-Shortwave Infrared Emission and Photodetection

Writing on Nanocrystals: Patterning Colloidal Inorganic Nanocrystal Films through Irradiation-Induced Chemical Transformations of Surface Ligands