Abstract:Background: Surface treatment of the intaglio surface of zirconia is important for bonding. However, it could affect the strength of the materials. The purpose of this study is to compare the effect of laser, etching, and air abrasion surface treatment methods to a control group on the flexural strength of three zirconia materials with two different thicknesses. (1) Methods: A total of 120 disks were divided into three groups according to the type of zirconia and the ceramic thickness. Then, according to the surface treatment method, the groups were divided into four subdivisions. The change in the microstructure of the ceramic material was investigated through Scanning Electron Microscope (EVO LS10, Carl Zeiss SMT Ltd. Oberkochen, Germany). Phase identification was performed using an X-ray diffraction device (XRD; Ultimate IV X-ray Diffractometer, Rigaku Inc., Tokyo, Japan). The flexural strength was assessed with a biaxial flexural strength test in a universal testing machine. Data were analyzed using SPSS Software (SPSS version 26.0.Armonk, NY: IBM Corp). A three-way ANOVA and a post hoc Dunnett T3 test were employed to evaluate the effect of the yttria concentration, thickness, and surface treatment on the flexural strength of zirconia (α = 0.05). (2) Results: At 0.8 mm thickness, air abrasion significantly increased the flexural strength of 3Y-TZP (1130.6 ± 171.3 MPa) and 4Y-TZP (872 ± 108.6 MPa). However, air abrasion significantly decreased the flexural strength of 5Y-TZP materials (373 ± 46.8 MPa). Laser irradiation significantly decreased the flexural strength of 5Y-TZP (347 ± 50.3 MPa), while etching significantly decreased the flexural strength of both 3Y-TZP (530 ± 48.8) and 4Y-TZP (457.1 ± 57.3). When the thickness increased to 1 mm, air abrasion continued to significantly decrease the flexural strength of 5Y-TZP materials. (3) Conclusions: There was a negative effect of surface treatment on the flexural strength at 0.8 mm thickness rather than at 1 mm thickness. Air abrasion enhances the flexural strength of 3Y-TZP and 4Y-TZP materials but significantly reduces the flexural strength of 5Y-TZP materials. Zircos-E etching and Er:YAG surface treatment methods did not significantly reduce the flexural strength of 5Y-TZP materials at 1 mm thickness and can be recommended as an alternative surface treatment for 5Y-TZP materials.

Influence of surface treatment of yttria-stabilized tetragonal zirconia polycrystal with hot isostatic pressing on cyclic fatigue strength

Cyclic fatigue resistance of yttria-stabilized tetragonal zirconia polycrystals with hot isostatic press processing

Effects of different surface treatments on the cyclic fatigue strength of one-piece CAD/CAM zirconia implants.

Cyclic fatigue behavior of Y‐TZP nanostructures with non‐homogeneous yttria distribution

Effect of the Intaglio Surface Treatment and Thickness of Different Types of Yttria-Stabilized Tetragonal Zirconia Polycrystalline Materials on the Flexural Strength: In-Vitro Study

Mechanical performance of Y-TZP monolithic ceramic after grinding and aging: Survival estimates and fatigue strength

Subcritical crack growth behavior and life data analysis of two types of dental Y-TZP ceramics

Exploration into the microstructural, mechanical, and biological characteristics of the functionally graded 3Y-TZP/Ti6Al4V system as a potential material for dental implants

Hot isostatic pressure treatment of 3D printed Ti6Al4V alters surface modifications and cellular response

Impact of the sintering parameters on the grain size, crystal phases, translucency, biaxial flexural strength, and fracture load of zirconia materials

Mechanical behavior and microstructural characterization of different zirconia polycrystals in different thicknesses

Topographical and crystalline change on surface by sandblasting improve flexural and shear bond strength of niobia-modified yttria-stabilized tetragonal zirconia polycrystal

The influence of hot isostatic pressing on precipitates, mechanical properties of Mg-12Gd-0.8Zn-0.4Zr (wt.%) alloy manufactured by sand casting

Properties of a Pressureless Sintered 2Y-TZP Material Combining High Strength and Toughness

Transient thermal stresses developed during speed sintering of 3 mol% yttria-stabilized tetragonal zirconia polycrystals

Impact of sandblasting on the flexural strength of highly translucent zirconia

Effects of microstructure characteristics on the tensile properties and fracture toughness of TA15 alloy fabricated by hot isostatic pressing

Microstructural and mechanical optimization of selective laser melted Ti6Al4V lattices: Effect of hot isostatic pressing

Fatigue performance of medical Ti6Al4V alloy after mechanical surface treatments

Effect of accelerated aging on dental zirconia-based materials

Herzian Contact Fatigue Test of Y-PSZ and Y-PSZ/Al2O3 Ceramics in Hot Water.