Optimized piezoelectric properties and temperature stability in PSN‐PMN‐PT by adjusting the phase structure and grain size
Feifei Guo,Chao Yang,Hongqiao Zhou,Shasha Dong,Pinyang Fang,Junjun Wang,Juan Du,Wei Long,Xiaojuan Li,Bin Yang,Zengzhe Xi
DOI: https://doi.org/10.1111/jace.18005
IF: 4.186
2021-07-21
Journal of the American Ceramic Society
Abstract:<p>For relaxor ferroelectric materials, improving the piezoelectric properties and temperature stability simultaneously is still a great challenge up to now. In this work, the structure, electric properties and thermal stability of <i>x</i>PSN-(1-<i>x</i>)PMN-0.4PT (<i>x</i> = 0.15, 0.29, 0.43 and 0.5) ceramics were studied systematacally by experiment and phase field simulation. A high Curie temperature <i>T</i><sub>c</sub> of 255 ℃ and good longitudinal electricmechanical coupling factor <i>k</i><sub>33</sub> of 0.75 and piezoelectric constant <i>d</i><sub>33</sub> of 650 pC/N are achieved in <i>x</i> = 0.43 ceramics with monoclinic C and tetragonal phases coexistence at room temperature. At 30 ℃, this composition ceramics sintered at 1260 ℃ shows the remnant polarization <i>P</i><sub>r</sub> and coercive field <i>E</i><sub>c</sub> are about 36.8 µC/cm<sup>2</sup> and 8.2 kV/cm, respectively. Moreover, as the temperature increases to 150 ℃, these values remain as high as 22.6 µC/cm<sup>2</sup> and 5.7 kV/cm. In the temperature range of 30 to 230 ℃, the variation of <i>k</i><sub>33</sub> and <i>d</i><sub>33</sub> is about 24% and 25%. These high piezoelectric performance and superior temperature stability are related to the more complex domain structures caused by phase coexistence and larger grains with more stable domain structure due to internal stress. The former is beneficial to improving the piezoelectric properties, and the latter dominates the enhanced temperature stability.</p>
materials science, ceramics