Demonstration of tritium adsorption on graphene

Genrich Zeller,Desedea Diaz Barrero,Paul Wiesen,Simon Niemes,Nancy Tuchscherer,Max Aker,Artus M. W. Leonhardt,Jannik Demand,Kathrin Valerius,Beate Bornschein,Magnus Schlösser,Helmut H. Telle

DOI: https://doi.org/10.1039/D3NA00904A

2024-04-10

Abstract:In this work, we report on studies of graphene exposed to tritium gas in a controlled environment. The single layer graphene on a $\textrm{SiO}_2$/Si substrate was exposed to 400 mbar of $\textrm{T}_2$ for a total time of $\approx$ 55 h. The resistivity of the graphene sample was measured $\textit{in situ}$ during tritium exposure using the Van der Pauw method. We found that the sheet resistance increases by three orders of magnitude during the exposure, suggesting significant chemisorption of tritium. After exposure, the samples were characterised $\textit{ex situ}$ via spatio-chemical mapping with a confocal Raman microscope, to study the effect of tritium on the graphene structure (tritiation yielding T-graphene), as well as the homogeneity of modifications across the whole area of the graphene film. The Raman spectra after tritium exposure were comparable to previously observed results in hydrogen-loading experiments, carried out by other groups. By thermal annealing we also could demonstrate, using Raman spectral analysis, that the structural changes were largely reversible. Considering all observations, we conclude that the graphene film was at least partially tritiated during the tritium exposure, and that the graphene film by and large withstands the bombardment by electrons from the $\beta$-decay of tritium, as well as by energetic primary and secondary ions.

Mesoscale and Nanoscale Physics

What problem does this paper attempt to address?

This paper mainly discusses the adsorption of tritium on graphene surfaces. The researchers exposed a single layer of graphene to tritium gas at approximately 400 millibars in a controlled environment for about 55 hours, and monitored the changes in its resistivity in real-time using the Van der Pauw method. The experiment found that the sheet resistance of graphene increased by three orders of magnitude, indicating significant chemical adsorption of tritium.

Subsequently, the researchers performed ex-situ characterization of the samples using confocal Raman microscopy to study the impact of tritium on the graphene structure (forming T-graphene) and the uniformity of modifications on the entire graphene film. Raman spectroscopy analysis revealed similar results to those observed in hydrogenation experiments, and through thermal annealing, they demonstrated that the structural changes were largely reversible.

The paper points out that the motivation for this research primarily comes from the field of astroparticle physics, particularly in relation to next-generation neutrino mass experiments such as KATRIN and PTOLEMY. These experiments require avoiding line broadening caused by tritium molecules in beta decay, in order to improve the sensitivity to neutrino mass. Therefore, the research team attempted to immobilize tritium atoms on graphene to form a solid tritium source, but faced the challenge of potential damage to the graphene structure caused by tritium and the scale-up of preparation.

In summary, this paper aims to experimentally demonstrate and understand the interaction between tritium and graphene, evaluate the feasibility of this system in large-scale tritium/carbon system applications, and explore the impact of tritium on the graphene structure and its reversibility.