Architecture Optimization Dramatically Improves Reverse Bias Stability in Perovskite Solar Cells: A Role of Polymer Hole Transport Layers

Fangyuan Jiang,Yangwei Shi,Tanka R. Rana,Daniel Morales,Isaac Gould,Declan P. McCarthy,Joel Smith,Grey Christoforo,Hannah Contreras,Stephen Barlow,Aditya D. Mohite,Henry Snaith,Seth R. Marder,J. Devin MacKenzie,Michael D. McGehee,David S. Ginger

2023-08-16

Abstract:We report that device architecture engineering has a substantial impact on the reverse bias instability that has been reported as a critical issue in commercializing perovskite solar cells. We demonstrate breakdown voltages exceeding -15 V in typical pin structured perovskite solar cells via two steps: i) using polymer hole transporting materials; ii) using a more electrochemically stable gold electrode. While device degradation can be exacerbated by higher reverse bias and prolonged exposure, our as-fabricated perovskite solar cells completely recover their performance even after stressing at -7 V for 9 hours both in the dark and under partial illumination. Following these observations, we systematically discuss and compare the reverse bias driven degradation pathways in perovskite solar cells with different device architectures. Our model highlights the role of electrochemical reaction rates and species in dictating the reverse bias stability of perovskite solar cells.

Chemical Physics

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the stability problem of perovskite solar cells under reverse bias. Specifically, reverse - bias instability is a key challenge faced by commercial perovskite solar cells, especially in tandem modules, where low - output solar cells (for example, due to partial shading) are forced to match the current output of other high - output solar cells, which may lead to local overheating and device performance degradation. This phenomenon is also a significant problem for silicon - based solar cell technology, but the reverse - bias breakdown voltage (VRB) of perovskite solar cells is usually low, ranging from - 0.5 V to - 3 V, far below the typical value of - 13 V for silicon - based solar cells. Therefore, improving the reverse - bias stability of perovskite solar cells is crucial for their practical applications.

By optimizing the device structure, especially by using a polymer hole - transport layer (HTL) and a more electrochemically stable gold (Au) electrode, the paper significantly improves the reverse - bias stability of perovskite solar cells, achieving a breakdown voltage of over - 15 V, a value comparable to that of silicon - based solar cells and much higher than that of perovskite solar cells with traditionally used silver (Ag) electrodes. In addition, the paper also explores the reverse - bias - driven degradation mechanism and proposes that electron injection plays an important role under reverse bias, and that a thick polymer HTL can not only suppress the oxidation reaction by slowing down the reduction reaction, but also reduce the possibility of local electrochemical degradation by flattening the transparent conductive oxide (TCO) contact surface. These findings provide new ideas and strategies for improving the reverse - bias stability of perovskite solar cells.