Consequences of Utilizing a Redox-Active Polymeric Binder in Li-ion Batteries

Sathish Rajendran,Haoyu Liu,Stephen E. Trask,Baris Key,Andrew N. Jansen,Marco-T. F. Rodrigues

DOI: https://doi.org/10.1016/j.jpowsour.2023.233584

2023-04-10

Abstract:Development of new polymeric binders can help enable the use of silicon-rich anodes in Li-ion batteries, by providing stronger adhesion to the active material particles. The compositional features that improve interfacial interactions and mechanical properties can often impart electronic conductivity and redox activity to these polymers, which are generally seen as beneficial to cell performance. Alternatively, it is also possible that the addition of charge-transferring centers to the electrode can accelerate cell degradation. Here, we use an aromatic polyimide (~320 mAh/g of reversible capacity) to explore how a redox-active conductive polymer can affect cell performance. We demonstrate that the lithiated polymer is less stable than the traditional binders upon storage, leading to increased rates of calendar aging. Furthermore, we show that the adhesion properties of the polymer deteriorate upon repeated cycling, to an extent that is proportional to the degree of delithiation of the binder. More critically, we show that progressive degradation of the redox behavior of the polymer leads to the release of extra Li+ into the cell, which can give the false perception of good performance even under conditions of poor stability. Our work suggests that redox-active conductive binders can sometimes be detrimental to cell performance, and that works evaluating new polymers must include careful experimental validation under realistic conditions.

Chemical Physics

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to evaluate the impact of using redox - active polymer binders on the performance of lithium - ion batteries. Specifically, the researchers used an aromatic polyimide (PI) as a model system to explore the consequences of applying this electrochemically active conductive polymer binder in lithium - ion batteries. The main concerns include:

1. **Electrochemical Activity of the Polymer Binder**: The electrochemical behavior of the PI binder was studied, especially its capacity change, Coulombic efficiency, and voltage - curve characteristics during the charge - discharge process. The results showed that the PI binder exhibited an extremely high capacity (about 1500 mAh/g) during the first lithiation, but the capacity rapidly decayed in subsequent cycles and finally stabilized at a lower level (such as 320 mAh/g).

2. **Stability of the Binder**: It was found that the PI binder has poor stability in the lithiated state, and long - term storage will accelerate the calendar aging of the battery. In addition, after multiple charge - discharge cycles, the adhesion performance of the PI binder will decrease significantly, which is proportional to the degree of delithiation.

3. **Release of Extra Lithium Ions**: The study also pointed out that the gradual degradation of the infrared characterization of the PI binder will lead to the release of "extra" lithium ions into the battery, which may cause a false improvement in battery performance, even in the case of poor stability.

4. **Problems in Practical Applications**: The paper emphasizes the problems that may be brought by using functional polymer binders in practical applications and suggests that strict experimental verification must be carried out when evaluating new polymer materials to ensure their performance and stability under real conditions.

In summary, this paper aims to reveal the potential advantages and disadvantages of redox - active conductive polymer binders in lithium - ion batteries through detailed research, providing a scientific basis for future design and optimization.