Influence of Gold-Selenium Precursor Ratio on Synthesis and Structural Stability of α- and β-AuSe

Aditya Kumar Sahu,Satyabrata Raj
2023-04-04
Abstract:Gold selenide (AuSe) is a multilayer compound yet to be thoroughly studied. The colloidal synthesis and characterization of gold selenide nanoparticles are described, emphasizing the effect of different gold-to-selenium precursor ratios and temperatures on the crystal structure and form. The structural characterization is done using an X-ray diffraction pattern. The coexistence of the {\alpha}- and {\beta}-AuSe phases is observed in all synthesized samples. The morphologies of the mainly {\alpha}-AuSe sample are nanobelts, whereas the primarily {\beta}-AuSe phase sample has a nanoplate-like structure, according to the TEM and SEM data. All of the samples had Raman vibrational modes with mixed phases. The effect of high pressure on as-prepared AuSe samples has been studied in this work. The introduction of external pressure and temperature allows both phases to transition. Pressure lowers the existence of other phase modes, and the corresponding dominating sample modes are entirely significant in our sample. The phase transition pressure was observed using Raman scattering. Our findings show that 2D AuSe has a lot of promise for multifunctional applications, encouraging more research on these systems.
Materials Science,Applied Physics
What problem does this paper attempt to address?
The problems that this paper attempts to solve are: to study the synthesis of gold selenide (AuSe) under different ratios of gold - selenium precursors and temperature conditions and its structural stability, especially the formation mechanisms of two crystal phases, α - AuSe and β - AuSe, and their phase - transition behaviors under high - pressure conditions. Specifically, the paper focuses on the following aspects: 1. **Influence of synthesis conditions**: - By changing parameters such as the ratio of gold to selenium precursors and the reaction temperature, study how these factors affect the crystal structure and morphology of AuSe nanomaterials. - The research found that different gold - selenium ratios and temperature conditions will lead to the co - existence of different proportions of the two phases, α - AuSe and β - AuSe. For example, at a lower temperature, a gold - rich environment is conducive to the formation of β - AuSe, while at a higher temperature, a selenium - rich environment is conducive to the formation of α - AuSe. 2. **Structural characterization**: - Use multiple means such as X - ray diffraction (XRD), transmission electron microscopy (TEM), field - emission scanning electron microscopy (FE - SEM), and Raman spectroscopy to perform structural characterization on the synthesized AuSe nanomaterials. - TEM images show that α - AuSe mainly presents a nano - ribbon - like structure, while β - AuSe mainly presents a nano - flake - like structure. 3. **Phase - transition behavior under high - pressure conditions**: - The changes in the Raman spectra of AuSe under high - pressure conditions were studied, and it was found that high pressure can promote the transformation between the two phases. As the pressure increases, some Raman peaks will experience red - shift or blue - shift, indicating that high pressure has a significant impact on the crystal structure of AuSe. - The results of high - pressure experiments show that applying external pressure can reduce the existence of other phase modes, making the dominant sample mode more prominent, thereby achieving the mutual conversion between the two phases. 4. **Potential applications**: - Research shows that as a two - dimensional material, AuSe has broad application potential, especially in fields such as optoelectronic devices, solar cells, and energy - storage systems. Its unique physical and chemical properties make it an ideal candidate material for future multi - functional devices. In summary, this paper aims to deeply understand the structural stability and phase - transition behavior of AuSe under different synthesis conditions, providing a theoretical basis for further developing its applications in advanced materials and devices.