Effect of shatterproof polymer film application on the fracture types and strength of glass subject to bending load

Tomohisa Kojima,Ryohei Momokawa,Takuma Matsuo,Mitsuo Notomi

DOI: https://doi.org/10.1016/j.engfailanal.2023.107220

2023-04-28

Abstract:Shatterproof polymer films are widely for windows used because they can be easily installed on existing glass windows to improve safety. Applying them to glass plates has been reported to not only prevent fragments from scattering but also increase load-bearing capacity and penetration resistance. However, the clarification of their mechanism and quantitative evaluation are still insufficient because the effect of film application on the strength and failure mode of glass under quasi-static loading has not been investigated. In this study, three-point bending tests and fracture surface observations were conducted on a float glass with a shatterproof polymer film. The stress field formed inside the glass was visualised during the tests using the photoelastic method. By varying the support span of the specimen, the deformation mode was varied to generate three types of failures: bending, shear caused by Hertzian contact stress, and mixed-mode failures. Under the conditions in the present study, the breaking loads of the specimens with and without film were almost the same; however, the fracture surface observation indicated that the area subjected to shear failure caused by Hertzian contact stress was larger with film application. Finally, the effect of the film thickness on the breaking load due to bending deformation was theoretically predicted.

Materials Science,Applied Physics

What problem does this paper attempt to address?

The paper primarily explores the impact of anti-shatter polymer films applied to glass on its fracture type and strength under bending loads. The study is conducted through three-point bending tests and observation of fracture surfaces. Specifically:

1. **Research Background**: Anti-shatter polymer films are widely used on window glass to enhance safety. These films not only prevent glass shards from scattering but also increase the load-bearing capacity and penetration resistance of the glass. However, the mechanism by which the film affects the strength of the glass and its fracture mode has not been fully elucidated.

2. **Research Methods**:
- Three-point bending tests and fracture surface observations were conducted, using photoelastic methods to visualize the stress fields formed inside the glass during the tests.
- Different types of fracture modes (bending fracture, shear fracture caused by Hertzian contact stress) were induced by changing the support span of the specimens.
- Theoretically predicted the effect of film thickness on the fracture load caused by bending deformation.

3. **Main Findings**:
- Under the conditions of this study, the fracture load of the specimens was almost the same regardless of whether the film was applied; however, fracture surface observations showed that the shear fracture area caused by Hertzian contact stress was larger when the film was applied.
- When the support span was large, the glass experienced bending fractures; when the support span was small, Hertzian fractures occurred; and at medium spans, a mix of both fracture modes (bending fracture and Hertzian fracture) appeared.
- For specimens with the film, the film was able to hold the glass fragments after fracture.

4. **Conclusion**: The study reveals how anti-shatter polymer films affect the fracture behavior of glass under bending loads, especially under different support span conditions. Although the application of the film has little impact on the fracture load of the specimens, it significantly changes the type and characteristics of the fracture, particularly in terms of Hertzian fractures.

In short, this paper, through experimental and theoretical analysis, delves into the impact of anti-shatter polymer films on the fracture behavior of glass and provides new insights into the behavior of this composite material.