Abstract:Fatigue delamination damage is one of the most important fatigue failure modes for laminated composite structures. However, there are still many challenging problems in the development of the theoretical framework, mathematical/physical models, and numerical simulation of fatigue delamination. What is more, it is essential to establish a systematic classification of these methods and models. This article reviews the experimental phenomena of delamination onset and propagation under fatigue loading. The authors reviewed the commonly used phenomenological models for laminated composite structures. The research methods, general modeling formulas, and development prospects of phenomenological models were presented in detail. Based on the analysis of finite element models (FEMs) for laminated composite structures, several simulation methods for fatigue delamination damage models (FDDMs) were carefully classified. Then, the whole procedure, range of applications, capability assessment, and advantages and limitations of the models, which were based on four types of theoretical frameworks, were also discussed in detail. The theoretical frameworks include the strength theory model (SM), fracture mechanics model (FM), damage mechanics model (DM), and hybrid model (HM). To the best of the authors' knowledge, the FDDM based on the modified Paris law within the framework of hybrid fracture and damage mechanics is the most effective method so far. However, it is difficult for the traditional FDDM to solve the problem of the spatial delamination of complex structures. In addition, the balance between the cost of acquiring the model and the computational efficiency of the model is also critical. Therefore, several potential research directions, such as the extended finite element method (XFEM), isogeometric analysis (IGA), phase-field model (PFM), artificial intelligence algorithm, and higher-order deformation theory (HODT), have been presented in the conclusions. Through validation by investigators, these research directions have the ability to overcome the challenging technical issues in the fatigue delamination prediction of laminated composite structures.

Progressive fatigue damage modeling of laminated composites using a novel combined fatigue life model

Continuum Damage Modeling and Progressive Failure Analysis of Carbon Fiber/epoxy Composite Pressure Vessel

Progressive fatigue damage modeling of laminated composites using strain-based failure criteria

Micromechanics-based Progressive Failure Analysis of Carbon FIber/epoxy Composite Vessel under Combined Internal Pressure and Thermomechanical Loading

Progressive Fatigue Modelling of Open-Hole Glass-Fibre Epoxy Laminates

Novel 2D strain-rate-dependent lamina-based and RVE/phase-based progressive fatigue damage criteria for randomly loaded multi-layer fiber-reinforced composites

Strength and stiffness degradation modeling and fatigue life prediction of composite materials based on a unified fatigue damage model

Progressive damage modelling and fatigue life prediction of Plain-weave composite laminates with Low-velocity impact damage

Fatigue life prediction of hybrid carbon-flax-epoxy laminates using progressive failure analysis and cohesive zone model

A 3D finite element model to simulate progressive damage in unidirectional- and woven-fibre thermoplastic discontinuous-long-fibre composites

Fuzzy fatigue life prediction of fiber-reinforced laminated composites by continuum damage mechanics

An Enhanced Progressive Damage Model for Laminated Fiber-Reinforced Composites Using the 3D Hashin Failure Criterion: A Multi-Level Analysis and Validation

Evaluation and Modeling of the Fatigue Damage Behavior of Polymer Composites at Reversed Cyclic Loading

Modeling of progressive high-cycle fatigue in composite laminates accounting for local stress ratios

Damage-entropy model for fatigue life evaluation of off-axis unidirectional composites

A unified damage model for fibrous composite laminae subject to in-plane stress-state and having multi material-nonlinearity

A progressive damage model for carbon fiber-reinforced polymer laminates subjected to fastener pull-through failure

Review and Assessment of Fatigue Delamination Damage of Laminated Composite Structures

Fatigue-driven failure criterion for progressive damage modelling and fatigue life prediction of composite structures

A Fatigue Model to Predict Interlaminar Damage of FRP Composite Laminates Subjected to Mode I Load

A critical plane approach for multiaxial fatigue life prediction of short fiber reinforced thermoplastic composites