Structure and electrochemistry of LixFeyNi1-yO2

J.N. Reimers,E. Rossen,C.D. Jones,J.R. Dahn,J Reimers

DOI: https://doi.org/10.1016/0167-2738(93)90401-n

IF: 3.699

1993-06-01

Solid State Ionics

Abstract:The solid solution series LiFeyNi1-yO2 (0.1≤y≤0.5) has been prepared from various starting materials. Using powder X-ray diffraction and Rietveld profile refinement, we show that this solid solution is only iso-structural with hexagonal LiNiO2 in the conposition range 0≤y≲0.23. For 0.23≲y≲0.48 phase coexistence occurs between hexagonal LiFe0.23Ni0.77O2 and cubic (NiO structure) LiFe0.48Ni0.52O2. For all samples in the hexagonal phase, cation mixing between transition metal and lithium layers, was observed. Using anomalous X-ray techniques we were able to determine that the cation mixing was primarily between Fe and Li. The cation mixing and the presence of the cubic phase for y>0.2, profoundly affects the electrochemical de-intercalation of Li from these materials. Electrochemical measurements using Li/Li1−xFeyNi1−yO2 cells show that as y increases the amount of Li which can be reversibly cycled, Δx, decreases, thus limiting the practical usefulness of these materials.

chemistry, physical,physics, condensed matter