Structure and Electrochemical Performance of LiNi(subscript Y)co(subscript (0.1-Y))mn1.9o4 Cathode Materials Prepared by a Precipitation Method

Guoguang Wang,Jianming Wang,Wenqu Mao,Li-Qing Liu,Jianqing Zhang,Chenzhong Cao

2005-01-01

Abstract:Spinel LiMn2O4 and LiNi(subscript y)Co(subscript (0.1-y))Mn1.9O4 (y=0, 0.05, 0.10) samples were prepared by a precipitation method. The structure, morphology, and electrochemical performance of the samples were characterized by Fourier transform infrared(FT-IR) spectroscopy, X-ray diffraction (XRD), scanning electron micrographs (SEM), charge-discharge measurements, and electrochemical impedance spectra (EIS). The results of FT-IR and XRD indicated that the absorption band at about 519cm^(-1) shifts to the high frequency with the decrease of Ni content in LiNi(subscript y)Co(subscript (0.1-y))Mn1.9O4 samples and the lattice parameter(a) of LiMn2O4 samples decreases with the addition of Ni, Co, or Ni/Co. The SEM observation dispplayed that the LiNi(subscript y)Co(subscript (0.1-y))Mn1.9O4 samples have lower agglomeration degree and smaller particle size. The results of the electrochemical experiments showed that the improvements on the electrochemical performance of substituted samples have some different reasons, and the LiNi0.05Co0.05Mn1.9O4 sample manifests better electrochemical performance in 4V region due to its lower electrochemical polarization and larger diffusion coefficient of Li(superscript +) ions.