Abstract:The severe oxidation of metal elements leads to a large amount of oxide inclusions that hinder the formation of metallurgical bonds across intersplat interfaces during thermal spraying in an ambient atmosphere, which further degrades the performance of thermally sprayed metal coatings. Controlling the oxidation of metal elements during spray deposition remains a significant challenge. In this paper, the thermodynamic and kinetic requirements of in-situ in-flight deoxidation by adding deoxidizer elements (diamond particles) to Fe / Al spray powders to achieve oxide-free molten droplets in an ambient atmosphere were investigated. Fe / Al / 2.5C composite powders containing 2.5wt.% diamond particles were prepared by mechanical alloying. Atmospheric plasma spraying (APS) was used to generate an oxide-free molten spray of FeAl particles at temperatures higher than 2 000 degrees C. This was achieved by the in-situ self-oxide cleaning effect of in-flight particles by carbon, which prevented metal droplets from oxidizing in an open atmosphere. For comparison, a FeAl coating was also deposited using Fe / Al composite powders prepared by mechanical alloying. The particle velocity and temperature were measured by a commercial thermal-spraying particle diagnostic system. The microstructures of the coatings were characterized by scanning electron microscopy and X-ray diffraction. The chemical compositions of the coatings were measured by inductively coupled plasma spectroscopy. The adhesive strength and hardness of the plasma-sprayed FeAl-based coatings were tested. The results show that under the combined effects of plasma- jet heating and the FeAl exothermic reaction, the heated FeAl spray particles could reach a high temperature of over 2 100 degrees C, which meets the thermodynamic conditions for carbon in-situ deoxidation. Because oxidation occurs from the surface of an in-flight molten droplet, to maintain continuous deoxidation of the molten FeAl droplet, the rapid transfer of carbon from the interior of the molten droplet to the surface is necessary. It was confirmed that the strong convection flow of the molten metal droplets satisfied the kinetic conditions of carbon in-situ in-flight deoxidation. The oxygen content in the APS-sprayed FeAl coatings increased with the increase of the spray distance. In contrast, the oxygen content in the APS-sprayed FeAl / 2.5C coatings decreased from 1.01 wt.% to 0.48 wt.% as the spray distance increased from 70 mm to 150 mm. This was accompanied by the decrease in carbon content from 1.41 wt.% to 0.31 wt.%, indicating the effective protection of Fe and Al from oxidation by the carbon in the droplet. Compared with the oxygen content of 3.67 wt.% in traditional FeAl coating, the oxygen content of the FeAl / 2.5C coatings was reduced to less than 0.5 wt.%. Considering that the carbon content of the coatings decreased as the spray distance increased, the results confirm that the in-flight oxidation of Fe and Al was suppressed by the preferential sacrificial oxidation of carbon in the molten droplets. Thus, the oxide in the FeAl / 2.5C coatings was mainly attributed to post-deposition oxidation. Moreover, the FeAl droplet reached the temperature to realize the spread-fusing self-metallurgical bonding effect for FeAl splats. The coatings exhibited a dense microstructure with an apparent porosity of less than 0.5%. The adhesive bonding strength of the prepared coatings exceeded 59.2 MPa owing to metallurgical bonding. The hardness of the coatings reached 590 HV0. 3, which was approximately twice that of traditional FeAl coatings. This was attributed to the reinforcement provided by the Fe3AlCx cementite phase resulting from the residual carbon in the coating.

Comparative Study on the Microstructure and Properties of 304 Stainless Steel Coatings Prepared by High-Velocity Oxygen Fuel Spraying and Air Plasma Spraying

Comparative Analysis on the Structure and Properties of Iron-Based Amorphous Coating Sprayed with the Thermal Spraying Techniques

The study of mechanical properties and corrosion behavior of the Fe-based amorphous alloy coatings using high velocity oxygen fuel spraying

Comparative Study on Corrosion Characteristics of Al2O3/316L and TiO2/316L Stainless Steel in Supercritical Water

Microstructure and Properties of Fe-based Amorphous Coating Prepared by High Velocity Spraying

Preparation of Different Coatings on 316 L Stainless Steel and their Corrosion Performance in Supercritical Water

Effect of Spraying Power on Microstructure, Corrosion and Wear Resistance of Fe-Based Amorphous Coatings

Surface coating of stainless steels by HVOF method and investigation of wear properties

Preparation of Aluminum Coatings by Atmospheric Plasma Spraying and Dry-Ice Blasting and Their Corrosion Behavior

Microstructure and Corrosion Study on Friction Surfaced Aluminum Alloy Coatings over Mild Steel

Wear and Corrosion of HVAF and HVOF-Sprayed WC-CoCr Coatings on Aluminum Alloy

Preparation process, surface properties and mechanistic study of HVAF-sprayed CoCrFeNiMo 0.2 high-entropy alloy coatings

Mechanism of Suppressing Oxidation of FeAl Molten Droplet by Adding C to Powder and Its Effect on Microstructure and Properties of Plasma-sprayed Coating

Microstructure and High Temperature Oxidation Resistance of FeMnCrAl/Cr3C2 Coatings Deposited by High Velocity Arc Spraying

Microstructure, Mechanical, and Corrosion Properties of 304 Stainless Steel-H13 Tool Steel Composite Cold Spray Coatings

Microstructure, spallation and corrosion of plasma sprayed Al2O3–13%TiO2 coatings

A Comparative Study on the Tribocorrosion Behaviors of AlFeCrNiMo High Entropy Alloy Coatings and 304 Stainless Steel

Development of Single-Stage TiNbMoMnFe High-Entropy Alloy Coating on 304L Stainless Steel Using HVOF Thermal Spray

Elevated-temperature wear behavior and mechanisms of APS-sprayed Al 0.6 TiCrFeCoNi high entropy alloy coating

Evaluation of corrosion and wear performance of Fe-based coating and hastelloy C276 in H 2 S environment on 304 stainless steel substrate

Microstructure and Tribological Performance of HVAF-Sprayed Ti-6Al-4V Coatings