Investigation of the Properties of High-Viscosity Modified Asphalt Binder under Hygrothermal Environments

Mingliang Xing,Guimin Li,Xiaowei Zhou,Huan Liu,Zhulin Cao,Zuzhong Li,Huaxin Chen
DOI: https://doi.org/10.3390/ma17122869
IF: 3.4
2024-06-13
Materials
Abstract:High-viscosity modified asphalt binder (HVMA) is used widely as a polymer-modified binder in porous asphalt pavement because it can improve the cohesiveness of the asphalt mixture. However, because of the high voidage in the mixture, HVMA is vulnerable to aging induced by temperature, oxygen, water, sunlight, and other climatic conditions, which degrades the performance of pavement. The properties of asphalt binder are affected adversely by the effects of hygrothermal environments in megathermal and rainy areas. Therefore, it is essential to study the aging characteristics of HVMA under the influence of hygrothermal environments to promote its application as a high-viscosity modifier. A hygrothermal cycle aging test (HCAT) was designed to simulate the aging of HVMA when rainwater was kept inside of the pavement after rainfall in megathermal areas. One kind of base bitumen and three kinds of HVMA (referred to as SBS, A, and B, respectively) were selected in this study. Short-term aging tests, hygrothermal cycling aging tests, and long-term aging tests were performed on the base bitumen and three kinds of modified asphalt binder. Fourier-transform infrared spectroscopy (FTIR), thermo-gravimetric analysis (TGA), and dynamic shear rheological (DSR) tests were used to evaluate the properties of the binders on the micro and macro scales. By comparing the index variations of the four binders before and after aging, the effects of the hygrothermal environment on the properties of HVMA were studied. It was found that the effects of the hygrothermal environment expedited the decomposition of the polymer and the formation of carbonyl groups compared with the TFOT and PAV test, which TGA confirmed further. Moreover, the thermal stability of the samples was improved after HCAT. In addition, the master curves of the complex modulus showed that hygrothermal cycles made the high-temperature rutting resistance of asphalt binder increase significantly. All of the results above verified that the effect of hygrothermal cycling could accelerate the aging of HVMA and shorten its service life.
materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter
What problem does this paper attempt to address?
This paper mainly discusses the performance changes of high viscosity modified asphalt under wet and hot conditions. The research team designed a simulated wet and hot cycle aging test (HCAT) to study the aging effects of high viscosity modified asphalt (HVMA) after rainwater stagnates in the pavement structure layer in hot and rainy areas. They selected the base asphalt SK-70 and three types of HVMA (referred to as SBS, A, and B) for short-term aging, wet and hot cycle aging, and long-term aging tests. The properties of these asphalts at the micro and macro levels were studied through Fourier Transform Infrared Spectroscopy (FTIR), Thermogravimetric Analysis (TGA), and Dynamic Shear Rheology (DSR), etc. The results showed that the wet and hot environment accelerated the decomposition of polymers and the formation of carbonyl groups, which was further confirmed by TGA, and the thermal stability of the samples improved after wet and hot cycling. DSR tests showed that wet and hot cycling significantly enhanced the high-temperature rutting resistance of asphalt. Therefore, wet and hot cycling accelerated the aging of HVMA, shortening its service life. The primary objective of the paper is to study the aging characteristics of HVMA in wet and hot environments, providing theoretical support for the degradation of drainage asphalt pavement performance in hot and rainy areas.