Microwave low-temperature treatment – Step leaching process for recovering black mass from spent lithium-ion batteries

Chao Liu,Jie Long,Yingying Gao,Hongwei Liu,Wei Luo,Xuegang Wang
DOI: https://doi.org/10.1016/j.jece.2023.109759
IF: 7.7
2023-03-30
Journal of Environmental Chemical Engineering
Abstract:Cathode materials in the black mass from spent lithium-ion batteries can be efficiently reduced using microwave treatment. However, the interaction of different components in the recovery process has not been fully understood. The study aims to reveal the influence of impurities on the recovery of valuable metals using microwave low-temperature roasting and step leaching, realizing the separation of impurities and valuable metals. The sample black mass containing impurities was obtained by industrial dismantling process. The mechanisms of microwave-enhanced reduction were revealed by studying the dielectric properties and thermal evolution of different elements. Dielectric loss tangent increased with temperature and reached a peak value of 0.12 at 550 °C, facilitating microwave absorption and reduction reactions. The cathode materials were reduced efficiently in a semi-closed microwave system without inert atmosphere. The impurities graphite, Al and organics (electrolyte and PVDF) were potential in-situ reducing agents. The reduction products consists of Li 2 CO 3 , CoO(Co) and a small amount of LiAlO 2 , LiF and CoF 2 . The co-leaching of Al and Co was observed during the carbonated water leaching for recovering Li 2 CO 3 , which can be precipitated as Co 6 Al 2 CO 3 (OH) 16 ·4H 2 O by aging of the leachate. Al in the water leaching residue was effectively removed using alkali leaching of 6 M NaOH. Finally, Co was selectively leached without dissolution of Cu by 2 M H 2 SO 4 . The optimized process parameters were obtained. The research results may provide technical guidance for the efficient recovery of industrial black mass.
engineering, chemical, environmental
What problem does this paper attempt to address?