Effect of preoxidation of titanium on the titanium–ceramic bonding

Min Yan,Chai-Tze Kao,Jyh-Siang Ye,Tsui-Hsien Huang,Shinn-Jyh Ding

DOI: https://doi.org/10.1016/j.surfcoat.2007.05.056

IF: 4.865

2007-01-01

Surface and Coatings Technology

Abstract:To improve the titanium–ceramic bonding is a challenged theme because the bonding plays an important role in long-term performance of dental prosthetic implants. This study focused on the pre-heat treatment effect on the surface characteristics of titanium and the bond strength of the porcelain–titanium system. Phase, morphology, and oxide layer thickness of the pre-heat-treated titanium were evaluated. In particular, the bond strength of porcelain fused to pre-treated titanium was measured by using three-point bending test. Statistical analyses were made using one-way analysis of variance (ANOVA). The results revealed that with an increase in treatment temperature, the intensity of diffraction peaks of rutile-type titania formed on pre-treated titanium surface increased. With regard to the thickness of the oxide layer, a monotonous change with increasing treatment temperature was observed. The bond strength of the porcelain–titanium system was 27.6 MPa for untreated titanium, which is above the minimum value of 25 MPa specified in ISO 9693 standard for the three-point bending test. When titanium subjected to pre-heat-treatment at 600–850 °C, the values became the range of 23.7–34.5 MPa, indicating significant differences (p<0.05). The highest value resided in the optimal pre-treatment temperature of 750 °C at which specimens also presented greater amounts of remained porcelains on the titanium side among all tested groups after bending test. On the basis of the data, the pre-heat treatment in air for titanium substrates might be a simple and effective method for strengthening the titanium–ceramic bonding.
[The Bonding Characteristic of Titanium and RG Experiment Porcelain].

Wei-hong Ren,Tian-wen Guo,Jie-mo Tian,Yun-long Zhang

DOI: https://doi.org/10.3760/j.issn:1002-0098.2003.04.023

2003-01-01

Abstract:OBJECTIVE:To study the bonding characteristic of Titanium and RG experiment porcelain. METHODS:5 specimens with a size of 10 mm x 5 mm x 1.4 mm were cast from pure titanium. Then 1 mm of RG experiment opaque and body porcelain were fused on the surface of the titanium specimens. The interface of titanium and porcelain was analyzed with a scanning electron microscope with energy-despersive spectrometry; 6 metal specimens with the size of 25 mm x 3 mm x 0.5 mm were cast from Ni-Cr alloy and a uniform thickness of 1 mm of VMK 99 porcelain was veneered on the central area of 8 mm x 3 mm 18 metal specimens as the same size were cast from pure titanium. The uniform thickness of 1 mm of VITA TITANKERAMIK porcelain, of Noritake super porcelain Ti-22 and of RG experiment porcelain were veneered on every 6 specimens respectively in the central area of 8 mm x 3 mm. The specimens were subjected to a three-point bending test on a load-test machine with a span of 20 mm, then the failure loads were recorded and statistically analysised. The RG porcelain/titanium crown was fabricated by fusing RG opaque porcelain and body porcelain to cast titanium substrate crown. RESULTS:The SEM results show no porosity and crackle were found in the interface. The energy-dispersive spectrometry show that there are Si, Ti and O in the 1 micro m layer between porcelain and titanium, which suggesting titanium and experiment porcelain bonding well. The three point test showed the fracture force for the combinations of titanium/VITA TITANKERAMIK porcelain, titanium/Noritake super porcelain Ti-22 and titanium/RG experiment porcelain were (7.233 +/- 2.539) N, (5.533 +/- 1.199) N and (6.316 +/- 1.433) N respectively. There were not statistically significant differences among them (t test, P < 0.01). The fracture force for the Ni-Cr alloy/VMK99 porcelain combination (12.733 +/- 3.297) N was significantly greater than those of the cast titanium/porcelain (t test, P > 0.05). The crown was translucent with no crack. CONCLUSION:RG porcelain is well compatible with titanium.
Effect of sputtering gold coating on the bonding strength between pure titanium and two low-fusing porcelains

Liang Rong,Xiaoping Luo,Ning Li,Zhigang Xie,Zhi Li,Xianzhi Shen

DOI: https://doi.org/10.11752/j.kqcl.2018.01.02

2018-01-01

Abstract:Objective To study the effect of sputtering gold coating on the bonding strength between pure titanium and two low-fusing porcelains according to the protocol of ISO 9693,and to characterize the titaniumporcelain interfaces.Methods Forty machined pure titanium samples were prepared according to the ISO 9693 protocol.Based on the type of sintering porcelains (SP:Super Porcelain Ti-22;TC:Triceram) and titanium base with or without sputtering gold (Au),forty titanium samples were divided equally into four groups (AuSP,AuTC,SP and TC group).Low-fusion dental porcelain was then sintered onto the titanium samples.Three-point bending test was performed to assess the bonding strength,and optical stereomicroscope was used to characterize the titanium-porcelain adhesion and determine the failure mode.The titanium-ceramic interface was examined by Field Emission Scanning Electron Microscope (FE-SEM) and Electron Micoporbe Analysis (EMPA).Results The bonding strength of the AuSP groups was much higher than that of the SP groups (P＜0.05),while no significant difference was found between AuTC group and TC group (P＞005).The SP,AuTC and TC groups showed predominately adhesive fracture,whereas the failure mode of AuTC group was mixture of cohesive and adhesive,mainly cohesive.FE-SEM with EMPA did not show visible cracks in the Au groups.The depth of titanium and oxygen diffusion was decreased in the presence of the gold coating.Conclusions Sputtering gold intermediate coatings can inhibit titanium and oxygen diffusion,improve the bonding strength between Super Porcelain Ti-22 system,but does not affect the bonding strength of Porcelain Triceram system.
Does the Serological Study for Viral Infection in Autoimmune Inner Ear Disease Make Sense?

J. García-Berrocal,R. Ramírez‐Camacho,J. González-García,J. Verdaguer,A. Trinidad

DOI: https://doi.org/10.1159/000111043

2008-02-01

ORL

Abstract:Viral infections of the labyrinth have been considered a major source of auditory and vestibular system pathology. However, the involvement of virus in the development of immune reactions responsible for immunomediated inner ear disease has not been studied enough. Following viral infection, an effector immune response, humoral (B cell) and/or cytotoxic (T cell) is directed against a virus and it might cross-react with self-protein or autoantigen, evoking an autoimmune response. Since clinically it can be very difficult to establish a viral etiology for such disorders, serologic studies can be used to confirm the suspected diagnosis. Patients affected by immunomediated inner ear disease that had presented an upper respiratory tract infection underwent an immunologic workup study including microbiological study. After the application of this diagnostic protocol, only one patient, that was subsequently diagnosed with Cogan’s syndrome, showed a positive serological test for viral infection. On the basis of the low efficacy of serological testing and due to the lack of evidence, we do not recommend to carry out serologic studies for viral infection.
Effects of heat treatment on the bonding strength of pure titanium processed via selective laser melting and porcelain

HU Dandan,LUO Xiaoping,REN Canxia

DOI: https://doi.org/10.12016/j.issn.2096-1456.2022.08.003

2022-01-01

Abstract:Objective To evaluate the effect of heat treatment on the bonding strength of pure titanium formed by selective laser melting (SLM) and porcelain. Methods Ninety-six pure titanium specimens were laser machined to meet ISO 9693 standards. The specimens were divided into a heat treated group (A) and a nonheat treated group (B). According to the porcelain type, the specimens in groups A and B were divided into Super Ti22 (a), Titankeramik (b), and Triceram (c) groups. Then, according to sandblasting pressures of 0.25 MPa (1) and 0.45 MPa (2), they were further divided into Aa1, Aa2, Ab1, Ab2, Ac1, Ac2, Ba1, Ba2, Bb1, Bb2, Bc1, and Bc2 groups. The surface morphology and roughness of the sandblasted specimens were assessed using a laser scanning confocal microscope. After the porcelain was fused, the three-point bending titanium-porcelain bonding strength was tested. A stereomicroscope was used to characterize the titanium-porcelain interfaces and determine the mode of failure. Results The Vickers hardness of group A specimens (188.21 ± 11.94) was significantly lower than that of group B specimens (204.48 ± 6.32) HV (P<0.05). The roughness value in group A1 (2.90 ± 0.32) μm was significantly lower than that in group A2 (3.43 ± 0.43) μm (P<0.05). Specimens in group B1 (2.62 ± 0.08) μm were significantly smaller than those in group B2 (3.01 ± 0.06) μm (P<0.05). The bonding strength in group Aa1 was (33.75 ± 2.31) MPa, group Aa2 was (36.32 ± 1.44) MPa, group Ab1 was (39.82 ± 2.28) MPa, group Ab2 was (33.74 ± 1.53) MPa and group Ac2 was (38.63 ± 1.36) MPa, which was significantly higher than that in the corresponding groups Ba1 (29.65 ± 1.10) MPa, Ba2 (27.17 ± 2.24) MPa, Bb1 (27.29 ± 1.61) MPa, Bb2 (23.85 ± 0.97) MPa, and Bc2 (35.75 ± 1.93) MPa (P<0.05). With increasing sandblasting pressure, the bonding strength of the titanium ceramic in group Aa2 was significantly higher than in group Aa1, while that in group Ab2 was significantly lower than that in group Ab1 (P<0.05). In groups A, Bc1 and Bc2, the fracture model showed mixed failure, while in groups Ba1, Ba2, Bb1, and Bb2, the model showed interfacial failure. Conclusion The Vickers hardness of SLM titanium can be significantly reduced by heat treatment. SLM pure titanium after heat treatment is beneficial to combination of the three porcelain types and titanium. The titanium-porcelain bonding strength may be affected by sandblasting pressure.
Hypochlorous Acid and Taurine-N-Monochloramine in Periodontal Diseases

A. Mainnemare,B. Mégarbane,A. Soueidan,A. Daniel,I. Chapple

DOI: https://doi.org/10.1177/154405910408301101

2004-11-01

Abstract:Chronic periodontitis is a multi-factorial disease involving anaerobic bacteria and the generation of an inflammatory response, including the production of metalloproteinases, pro-inflammatory cytokines, and eicosanoids. Hypochlorous acid (HOCl) and taurine-N-monochloramine (TauCl) are the end-products of the neutrophilic polymorphonuclear leukocyte (PMN) respiratory burst. They act synergistically to modulate the inflammatory response. In the extracellular environment, HOCl and TauCl may directly neutralize interleukin 6 (IL-6) and several metalloproteinases, while HOCl increases the capacity of α2-macroglobulin to bind Tumor Necrosis Factor-alpha, IL-2, and IL-6, and facilitates the release of various growth factors. TauCl inhibits the production of inflammatory mediators, prostaglandins, and nitric oxide. HOCl activates tyrosine kinase signaling cascades, generating an increase in the production of extracellular matrix components, growth factors, and inflammatory mediators. Thus, HOCl and TauCl appear to play a crucial role in the periodontal inflammatory process. Taken together, these findings may offer opportunities for the development of novel host-modulating therapies for the treatment of periodontitis.
[Effect of Sintering Gold Paste Coating on the Bonding Strength of Pure Titanium and Three Low-Fusing Porcelains].

Ya-li Zhang,Xiao-ping Luo,Li Zhou

DOI: https://doi.org/10.3760/cma.j.issn.1002-0098.2012.05.005

2012-01-01

Abstract:OBJECTIVE:To study the effect of sintering gold paste coating of pure titanium on the adhesion of three porcelains following the protocol ISO 9693, and to investigate the titanium-porcelains interfaces. METHODS:Sixty machined pure titanium samples were prepared in a rectangular shape according to ISO 9693 and divided equally into six groups. Half of the strips were coated with gold paste (Deckgold) and sintered. Three ultra-low-fusing dental porcelains (I: Initial Ti, S: Super porcelain Ti-22, T: TitanKeramik) were fused onto the titanium surfaces. A thin layer of bonding agent was only applied on the surfaces of uncoated gold specimens. The interface of the porcelain and titanium was observed with a field emission scanning electron microscope (FE-SEM) after metallographic preparation and sputtered with a very thin carbon layer of the embedded titanium-porcelain interface. After three-point bending test was performed, optical stereomicroscope was used to characterize the titanium-porcelains adhesion and determine the mode of failure. RESULTS:FE-SEM illustrated intermetallic compounds of Au-Ti formed with some visible microcracks in the gold layer and the interface of gold layer and ceramic. All the uncoated gold titanium-porcelain system showed predominately adhesive fracture at the titanium oxidation, whereas the failure modes in all gold coated systems were cohesive and adhesive, mainly cohesive. The three-point-bending test showed that the bonding strength of GS and GI groups [(37.08 ± 4.32) and (36.20 ± 2.40) MPa] were higher than those in uncoated groups [(31.56 ± 3.74) and (30.88 ± 2.60) MPa, P < 0.05], while no significant difference was found between T group and GT group (P > 0.05). CONCLUSIONS:The gold paste intermediate coatings can improve bond strengths of Super porcelain Ti-22 system and Initial Ti system, which have potential applications in clinical fields.
Study on the interface of Ti-porcelain fused under different surface treatment]

Yang Liu,Yong-lie Chao,Xiao-dong Chen,De-peng Li,Min-jie Fu,Lei Cong

DOI: https://doi.org/10.3969/j.issn.1672-173x.2005.04.034

2005-01-01

Abstract:This study was made to observe the topography and ionic diffusion of the elements titanium, silicon, et cetera in the Ti-porcelain interface area which was pretreated with different methods.Ti-bond porcelain was fused on commercial pure titanium (CPT) with 8 different pretreatment methods; according to the temperature of the preoxidation, there were 300 degrees C, 400 degrees C, 500 degrees C and 600 degrees C groups, and based on the oxidizing-time in the air, there were 5 min, 15 min, 2 h and 24 h groups. The topography and ionic diffusion of elements in the Ti-porcelain interface area were observed with scanning electron microscopy (SEM) and electron probe microanalysis (EPMA) respectively.There were clefts and exfoliations in the 500 degrees C pre-oxidation group and 600 degrees C pre-oxidation group in SEM images. The distribution of titanium in the interlayer in EPMA images decreased from the titanium surface to porcelain, which was opposite to the distribution of silicon.The clefts and exfoliations suggested the position of the fracture and brittleness of alpha-Ti[o] layer. The widths of ionic diffusion in the eight groups were different, but it was difficult to measure and compare them exactly.
[Disorders of the blood composition in acute leukemias; biological and therapeutic study].

J. Soulier,J. Dausset

Abstract:
Corrosion Resistance and Ion Dissolution of Titanium Implant under Different Temperature Thermal Oxidation

严洪海,赵士芳,陈关福

DOI: https://doi.org/10.3969/j.issn.1007-3957.2001.03.004

2001-01-01

Abstract:Objective: In vitro corrosion resistance and ion dissolution of titanium implants. Methods: Three different kinds of thermal treatments were investigated using adopting constant potential meter and atomic absorption spectroscopy. Results:The treatments were natural oxidation(c. p. Ti), artificial oxidation(400 ℃,45min), high temperature oxidation(700℃,45min).It was discovered that each group of surfaces all have good corrosion resistance and low ion release rate. Among them, the corrosion resistance of artificial oxidation group was the best, the titanium ion release rate was the lowest, while the corrosion resistance of natural oxidation group was the worst and its titanium ion release rate was the highest.Conclusion:The surface of artificial oxidation group had the best stability.
Modified thermal mismatch value Δα for evaluating thermal compatibility of multi-layer dental ceramic composites

CUI Jun,LIU Xueheng,MA Lian

2010-01-01

Abstract:Objective The purpose of this study was to use polynomial function ΔL/L= C+α1 T+α2 T2 to describe the thermal contraction behavior of dental porcelain. In addition,modified Δα method was proposed to evaluate thermal compatibility.Methods The thermal contraction curve of one dental alloy,two ceramic core and nine veneering porcelains were measured on cooling from 470℃ to 20℃ by means of a vertical differential pushrod thermal dilatometer. An equation was deduced to calculate thermal mismatch value (Δα) between substrate and veneer. Discs of eight substrate/veneer combinations (n=10) were fabricated for thermal shock testing. A regression analysis was performed to determine the relationship between the results of thermal shock test and the thermal mismatch value (Δα) on these combinations.Results In this study,all the ceramics showed non linear dimensional change during cooling. A high degree of correlation (R=0.817) was found between thermal shock test results and thermal mismatch value (Δα).Conclusion Modified thermal mismatch value (Δα) is a promising approach for evaluation of thermal compatibility between substrate and veneer porcelain.
QUALIDEM: development and evaluation of a dementia specific quality of life instrument––validation

T. Ettema,R. Dröes,J. de Lange,G. Mellenbergh,M. Ribbe

DOI: https://doi.org/10.1002/gps.1692

2007-05-01

International Journal of Geriatric Psychiatry

Abstract:To validate the QUALIDEM, a quality of life measure for people with dementia within residential settings rated by professional caregivers.
Effects of posttreatment on the metal-ceramic bond properties of selective-laser-melted Co-Cr dental alloy—Part 2: Heat treatment after porcelain firing

Yanan Zhou,Xin Dong,Ning Li,Jiazhen Yan

DOI: https://doi.org/10.1016/j.prosdent.2023.01.030

2023-03-01

Abstract:STATEMENT OF PROBLEM: The selective laser melting (SLM) technique has been a promising method of fabricating Co-Cr metal-ceramic restorations; however, the lower metal-ceramic bond properties of SLM Co-Cr restorations have become a major issue in clinical use.PURPOSE: The purpose of this in vitro study was to propose and verify a method of improving the metal-ceramic bond properties of SLM Co-Cr alloy with heat treatment after porcelain firing (PH).MATERIAL AND METHODS: Forty-eight (25×3×0.5 mm) Co-Cr specimens, divided into 6 groups (Control group [CG]; 550 °C; 650 °C; 750 °C; 850 °C; 950 °C) according to PH temperatures, were prepared by using SLM techniques. The 3-point bend tests were performed to evaluate the metal-ceramic bond strengths; subsequently, the fracture feature was assessed by using a digital camera and scanning electron microscope (SEM) coupled with an energy-dispersive X-ray spectroscopy (EDS) detector, to determine the area fraction of adherence porcelain (AFAP). The interface morphologies and element distribution were determined with SEM/EDS detectors. Phase identification and quantification were examined with an X-ray diffractometer (XRD). A 1-way ANOVA and the Tukey honestly significant difference tests were used to analyze bond strengths and AFAP values (α=.05).RESULTS: The bond strengths were 35.33 ±1.25 MPa for the CG group, 34.53 ±3.20 MPa for the 550 °C group, 38.20 ±2.60 MPa for the 650 °C group, 42.85 ±2.31 MPa for the 750 °C group, 33.28 ±3.85 MPa for the 850 °C group, and 29.09 ±2.86 MPa for the 950 °C group. Significant differences were not observed among the CG, 550 °C, and 850 °C groups (P>.05) but were found among the other groups (P<.05). Fracture and AFAP results displayed a mixed fracture mode of adhesive and cohesive fracture. The thicknesses of native oxide films across the 6 groups were relatively close as the temperature increased, but the thickness of the diffusion layer increased as well. Excessive oxidation and massive phase transformation caused holes and microcracks to appear in the 850 °C and 950 °C groups, reducing bond strengths. XRD analysis evidenced that the phase transformation of γ→ε occurred at the interface during PH treating.CONCLUSIONS: PH treatment significantly affected the metal-ceramic bond properties of SLM Co-Cr porcelain specimens. The 750 °C-PH-treated specimens displayed higher mean bond strengths and improved fracture characteristics among the 6 groups.

dentistry, oral surgery & medicine
Compatibility of Ce-TZP/Al2O3 nanocomposite frameworks and veneering porcelains

Yuichi Terui,Kotaro Sato,Daisuke Goto,Yasuhiro Hotta,Yukimichi Tamaki,Takashi Miyazaki

DOI: https://doi.org/10.4012/dmj.2012-039

Abstract:The aim of this study was to examine the compatibility of Ce-TZP/Al2O3 nanocomposite (CTA) frameworks and veneering porcelains using the Schwickerath crack initiation test and clarify the effects on debonding/crack initiation strength (DIS) of both surface pretreatment (include heat treatment) of the frameworks, type of veneering porcelain varying the coefficient of thermal expansion (CTE), and surface roughness of the frameworks. The surfaces of Ce-TZP/Al2O3 plates were mechanically treated and followed by post-heat treatment. The liner and body porcelains were built up and fired according to the manufacturer's instructions. Surface analyses of the fractured plates showed compatibility with liner porcelains. Since no statistically difference in the DIS was found amongst the different surface treatments, post-heat treatments don't be mandatory. Whereas, since differences in DIS were found when different porcelains with different CTE were used, we concluded the matching of CTE of the porcelain with that of Ce-TZP/Al2O3 was important for successful all-ceramic restorations using Ce-TZP/Al2O3 frameworks.
Effect of Surface Treatment on the Three-Point Bend Bonding Strength Between Pure Titanium Fabricated by Selec-Tive Laser Melting and Porcelain

Dan-Dan Hu,Can-Xia Ren,Xiao-Ping Luo

DOI: https://doi.org/10.19439/j.sjos.2023.03.002

2023-01-01

Abstract:PURPOSE:To evaluate the effect of surface treatment on bonding strength between pure titanium formed by selective laser melting and porcelain.METHODS:Pure titanium strips (64) and cobalt-chromium alloy strips (16) were laser machined to meet ISO 9693 standards. The pure titanium specimens were divided into 4 groups according to the sandblasting pressure and interlayer material. The sandblasting pressure of 0.25 MPa of bonder porcelain group was TB1, the sandblasting pressure of 0.25 MPa of gold coating group was TG1, the sandblasting pressure of 0.45 MPa of bonder porcelain group was TB2, and the sandblasting pressure of 0.45 MPa of the gold coating group was TG2(n=16). After porcelain fusing, half of the specimens in each group were tested for three-point bend bonding strength, and the other half were tested after 10 000 cycles of thermal cycling(n=8). The bonding strength of cobalt-chromium alloy after sandblasting at 0.25 MPa and 0.45 MPa was taken as the control group and recorded as group C1, C2(n=8). The bonding strength was tested using classical three-point bending experiment. The surface roughness of pure titanium was measured by laser scanning confocal microscope(LSCM). Field emission scanning electron microscopy(FE-SEM) was used to observe the interface morphology of titanium-ceramic. The surface morphology of titanium after porcelain stripping was observed with stereomicroscope and fracture modes were analyzed by it. Graphpad Prism 8.0 software package was used for statistical analysis of the data.RESULTS:The bonding strength of group TG2 was (40.16±3.97) MPa and (37.38±2.39) MPa of group TG1, which were significantly higher than that of group TB2 (36.32±1.44) MPa and group TB1 (33.75±2.31) MPa (P＜0.05). The bonding strength of group TB2 with 0.45 MPa sandblasting was significantly higher than that of group TB1 with 0.25 MPa sandblasting (P＜0.05). There was no significant decrease in titanium-ceramic bonding strength before and after thermal cycling. When the sandblasting pressure increased from 0.25 MPa to 0.45 MPa, the roughness increased significantly (P＜0.05). The fracture modes were mixed.CONCLUSIONS:Under the conditions of this study, gold coating can significantly improve the bonding strength of Ti22 porcelain and SLM pure titanium than bonder porcelain, and increase of sandblasting pressure can further improve the bonding strength of titanium-porcelain. After 10 000 cycles of thermal cycling, the titanium-porcelain bonding strength did not decrease significantly.
In Vitro Investigation of the Wear of Human Enamel by Dental Porcelain

KT Metzler,RD Woody,AW Miller,BH Miller

DOI: https://doi.org/10.1016/s0022-3913(99)70280-5

1999-01-01

Abstract:Statement of problem. Metal ceramic systems are advocated when both esthetics and strength are required. A major drawback to many porcelains is their wear and destruction of opposing natural dentition. Purpose. This study evaluated the wear of enamel opposing 1 traditional and 2 recently introduced low-fusing feldspathic dental porcelains. Material and methods. Six blocks of Ceramco II, Finesse, and Omega 900 feldspathic porcelain materials were fabricated and fired according to manufacturer recommendations. Porcelain blocks were polished through 0.25 μm diamond polishing paste. Thirty-six enamel specimens were obtained and milled to a 2 mm (+0.5 mm) diameter. Enamel specimens were attached to an offset cam motor operating at 60 Hz. Enamel specimens were in constant contact with the stationary porcelain blocks under a load of 600 g and traversed a distance of 8 mm. Diameter and height of enamel specimens were measured at times of 0, 6, 12, 24, and 48 hours and subsequent determination of enamel volume loss recorded. Profilometric surface roughness of the ceramic blocks was also measured for the corresponding times. Results. Statistical analysis revealed that both Finesse and Omega 900 feldspathic porcelains caused significantly less enamel volume loss when compared with Ceramco II porcelain at all time intervals. Surface roughness revealed no consistent significant differences among porcelains. Conclusion. Both Finesse and Omega 900 porcelains were not as destructive to human tooth structure as Ceramco II porcelain. These results suggest an advantage of the new, lower-fusing porcelains in conditions where natural dentition wear is a concern. (J Prosthet Dent 1999;81:356-64.)
A study on thermal compatibility between alumina glass-infiltrated core/vintage AL veneering porcelain

Cui Jun,Liu Xueheng,Ma Lian,Chao Yonglie,Jia Li

2008-01-01

Abstract:Objective The purpose of this study is to evaluate the thermal compatibility between alumina glass-infiltrated core and the veneering porcelain. Methods Rectangular bar shaped specimens (25mm×5.0mm×5.0 mm) of the alumina glass-infiltrated core,AL veneering materials,including body porcelain and opaque were fabricated. The dilatometric data of all the specimens were measured at a temperature range of 500-25℃. Results The thermal contraction coefficient of the alumina glass-infiltrated core,body porcelain and opaque were 7.6×10-6 ℃,6.7×10-6 ℃,7.1×10-6 ℃,respectively. Conclusion Vintage AL veneering porcelain has good thermal compatibility with the alumina glass-infiltrated core ceramic.
[The shear bond strength of porcelain and base metal alloys for metal-ceramic crown (VII)]

C S Hsu,Y T Wu

Abstract:The popularity of the base metal alloys has increased in the past decade because of their lower price, high tensile strength and high elastic modulus. Several factors are critical in ensuring successful bonding: the matching of the thermal coefficients of expansion and constraction of the porcelain and metal, the metallurgic composition of the alloy and the pretreatment procedures used in preparation of the metal substructure. Two ceramic base alloys (one alloy contains beryllium, another without) were studied. The surface textures were created by 50 microns, 100 microns aluminum oxide sandblasting, carbide bur, carborundum point and disk upon two base alloys, Rexillium III and Wiron 88. The purposes of this investigation were to determine how these variations in surface texture affect the bond strength of the two ceramo-metal alloy systems. The following results were obtained: 1. Statistics revealed that bond strength was not significantly increased with surface roughness (p > 0.05). 2. The shear bond strength for variable pretreatment methods were in the following sequence: 100 microns Al2O3 sandblasting, carbide bur, 50 microns Al2O3 sandblasting, carborundum point, disk. 3. The Rexillium III alloy had a significantly higher bond strength than Wiron 88 alloy (p < 0.05). 4. The Noritake porcelain showed a significantly higher bond strength than Biobond porcelain (p < 0.05). 5. The fracture site was cohesive and adhesive mode treated with 50 microns Al2O3, 100 microns Al2O3, carbide bur. But carborundum point and disk was adhesive mode.
Concise Review Biomaterials & Bioengineering: Fusing of Dental Ceramics to Titanium

M. Könönen,J. Kivilahti

DOI: https://doi.org/10.1177/00220345010800030101

2001-03-01

Journal of Dental Research

Abstract:Titanium is known as a useful biometal because of its good biocompatibility and mechanical performance. However, titanium is chemically an exceptional metal, reacting strongly with gaseous elements like oxygen, hydrogen, and nitrogen and also dissolving them extensively. This high reactivity causes problems, for example, when dental ceramics are fused to titanium. Commercial ceramic-titanium systems are increasingly used in prosthetic dentistry, but little is known about the microstructure and composition of the system. Better understanding of chemical reactions between ceramics and titanium is necessary if mechanically more compatible ceramic-titanium bonds are to be developed. This review deals with titanium as a metal, titanium's affinity for non-metallic elements (especially oxygen), and reactions with other elements. Different aspects are discussed relative to the fusing of dental ceramics to titanium.

dentistry, oral surgery & medicine

Regulation of MMP-2 gene transcription in dermal wounds.

Effect of preoxidation of titanium on the titanium–ceramic bonding

[The Bonding Characteristic of Titanium and RG Experiment Porcelain].

Effect of sputtering gold coating on the bonding strength between pure titanium and two low-fusing porcelains

Does the Serological Study for Viral Infection in Autoimmune Inner Ear Disease Make Sense?

Effects of heat treatment on the bonding strength of pure titanium processed via selective laser melting and porcelain

Hypochlorous Acid and Taurine-N-Monochloramine in Periodontal Diseases

[Effect of Sintering Gold Paste Coating on the Bonding Strength of Pure Titanium and Three Low-Fusing Porcelains].

Study on the interface of Ti-porcelain fused under different surface treatment]

[Disorders of the blood composition in acute leukemias; biological and therapeutic study].

Corrosion Resistance and Ion Dissolution of Titanium Implant under Different Temperature Thermal Oxidation

Modified thermal mismatch value Δα for evaluating thermal compatibility of multi-layer dental ceramic composites

QUALIDEM: development and evaluation of a dementia specific quality of life instrument––validation

Effects of posttreatment on the metal-ceramic bond properties of selective-laser-melted Co-Cr dental alloy—Part 2: Heat treatment after porcelain firing

Compatibility of Ce-TZP/Al2O3 nanocomposite frameworks and veneering porcelains

Effect of Surface Treatment on the Three-Point Bend Bonding Strength Between Pure Titanium Fabricated by Selec-Tive Laser Melting and Porcelain

In Vitro Investigation of the Wear of Human Enamel by Dental Porcelain

A study on thermal compatibility between alumina glass-infiltrated core/vintage AL veneering porcelain

[The shear bond strength of porcelain and base metal alloys for metal-ceramic crown (VII)]

Concise Review Biomaterials & Bioengineering: Fusing of Dental Ceramics to Titanium