Abstract:Cerium substituted yttrium iron garnet (Ce:YIG) epitaxial thin films are prepared on gadolinium gallium garnet (GGG) substrate with pulsed laser deposition (PLD). It is observed that the films grown on GGG(111) substrate exhibit perpendicular magnetic anisotropy (PMA) as compared to films grown on GGG(100) substrate. The developed PMA is confirmed from magneto-optical Kerr effect, bulk magnetization and ferromagnetic resonance measurements. Further, the magnetic bubble domains are observed in the films exhibiting PMA. The observations are explained in terms of the growth direction of Ce:YIG films and the interplay of various magnetic anisotropy terms. The observed PMA is found to be tunable with thickness of the film and a remarkable temperature stability of the PMA is observed in all the studied films of Ce:YIG deposited on GGG(111) substrate.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: to achieve stable perpendicular magnetic anisotropy (PMA) in cerium - substituted yttrium iron garnet (Ce:YIG) epitaxial films. Specifically, the authors prepared Ce:YIG films on different substrate orientations by optimizing the growth conditions of pulsed - laser deposition (PLD) and studied the magnetic properties of these films. They found that when using a (111) - oriented gadolinium gallium garnet (GGG) substrate, the grown Ce:YIG films exhibited significant PMA, while the films grown on a (100) - oriented GGG substrate did not have this property. ### Main problems and solutions 1. **Problem**: How to achieve and stabilize PMA in Ce:YIG films? - **Solution**: PMA was successfully achieved by optimizing the growth conditions of PLD, especially the substrate temperature and substrate orientation. Experiments showed that only the films grown on GGG(111) substrates had obvious PMA, and this PMA remained stable in a wide temperature range (≤400 K). 2. **Problem**: What is the specific mechanism of PMA? - **Solution**: The existence of PMA was confirmed by multiple characterization methods (such as magneto - optical Kerr effect, bulk magnetization measurement, and ferromagnetic resonance), and its origin was explained by combining theoretical analysis. Research showed that the formation of PMA was related to the growth direction of the film and the interaction of various magnetic anisotropies, including intrinsic magnetocrystalline anisotropy, magnetoelastic anisotropy, and shape anisotropy, etc. 3. **Problem**: How is the temperature stability of PMA? - **Solution**: Through temperature - dependent P - MOKE measurements, it was confirmed that PMA remained stable in the temperature range from 80 to 460 K, which provided an important basis for practical applications. ### Key conclusions - Ce:YIG films exhibited significant PMA on GGG(111) substrates, and this PMA remained stable in a wide temperature range. - The formation of PMA was closely related to the growth direction of the film and the substrate orientation, especially the GGG(111) substrate played a key role in the formation of PMA. - By optimizing the PLD growth conditions, the intensity and temperature stability of PMA can be effectively regulated, thus making it possible for the practical application of Ce:YIG films. ### Formula summary The formulas involved in the paper mainly include: - **Effective PMA field \(H_K\)**: \[ H_{Sat} = H_K - 4\pi M_S \] where \(H_{Sat}\) is the in - plane saturation field and \(M_S\) is the saturation magnetization. - **Anisotropic energy density \(K_U\)**: \[ K_U=\frac{H_K M_S}{2} \] - **Magnetoelastic anisotropy density \(K_{ME}\)**: \[ K_{ME}=\left(\frac{9}{4}\right)\lambda_{111}C_{44}\left(\frac{\pi}{2}-\beta\right) \] where \(\lambda_{111}\) is the magnetostrictive coefficient, \(C_{44}\) is the shear modulus, and \(\beta\) is the shear distortion angle. These results indicate that through appropriate optimization of growth conditions, stable PMA can be achieved in Ce:YIG films, which provides a new material choice for the fields of magnetism and spintronics.

Robust perpendicular magnetic anisotropy in Ce substituted yttrium iron garnet epitaxial thin films

Epitaxial Growth of Y3fe5o12 Thin Films with Perpendicular Magnetic Anisotropy

Role of Cerium Doping on Epitaxial Yttrium Iron Garnet Thin Films

Magnetism and Magneto-optical Effects in Bulk and Few-layer CrI$_3$: A Theoretical GGA + U Study

Polycrystalline to preferred-(100) single crystal texture phase transformation of yttrium iron garnet nanoparticles

Pulsed laser deposition of epitaxial yttrium iron garnet films with low Gilbert damping and bulk-like magnetization

Control of magnetization dynamics by substrate orientation in YIG thin films

Nanometer-Thick Yttrium Iron Garnet Films with Perpendicular Anisotropy and Low Damping

Preparation of Ce-substituted yttrium iron garnets (Ce:YIG)

Strain-induced perpendicular magnetic anisotropy and Gilbert damping of Tm3Fe5O12 thin films

Perpendicularly magnetized YIG films with small Gilbert damping constant and anomalous spin transport properties

Ferromagnetic Resonance Studies of Strain tuned Bi:YIG Films

Evolution of microstructure, magnetic and microwave properties of sputter deposited polycrystalline YIG thin films

Single-crystal epitaxial europium iron garnet films with strain-induced perpendicular magnetic anisotropy: structural, strain, magnetic, and spin transport properties

A Strategy for Enhancing Perpendicular Magnetic Anisotropy in Yttrium Iron Garnet Films

Patterned growth of crystalline Y$_{3}$Fe$_{5}$O$_{12}$ nanostructures with engineered magnetic shape anisotropy

Strain-induced magnetic anisotropy of REIG thin films grown on YAG(111) substrates by pulsed laser deposition

Effects of post-deposition annealing on the structure and magnetization of PLD grown Yttrium Iron Garnet films

Supplemental Materials for “ Photo-Spin-Voltaic Effect ”

Bismuth Doping Enhanced Tunability of Strain-Controlled Magnetic Anisotropy in Epitaxial Y3Fe5O12(111) Films

Sputtered terbium iron garnet films with perpendicular magnetic anisotropy for spintronic applications