Ion irradiation effect on mechanical properties and corrosion resistance of a Cu 50 Zr 50 metallic glass

Zida Zhang,Pengcheng Che,Jian Zhang,Hongbo Fan,Zhiliang Ning,Jianfei Sun,Yongjiang Huang

DOI: https://doi.org/10.1002/adem.202101765

IF: 3.6

2022-04-05

Advanced Engineering Materials

Abstract:The effect of H+ ion irradiation on the structure and properties of a Cu50Zr50 metallic glass (MG) was investigated. High energy synchrotron X‐ray diffraction results indicate that the glass maintains its amorphous nature after ion irradiation. As the ion fluence increases, the atomic bond length of MGs becomes shorter, whereas the nanohardness and Young's modulus increase from 7.08±0.01 GPa and 111.3±1.1 GPa for the as‐spun sample to 8.59±0.06 GPa and 123.1±1.3 GPa for the sample irradiated with 2×1016 cm‐2 fluence. The corrosion potential of the studied MG in 1 mol/L HCl increases from ‐0.5953 V to ‐0.4519 V, suggesting an enhanced corrosion resistance of MGs after ion irradiation. The modification of mechanical properties and corrosion resistance can be interpreted from the ion irradiation‐induced structural evolution. The results obtained here can be beneficial for better understanding the mechanical properties and corrosive behaviors of MGs under extreme conditions like ion irradiation and thus promoting their industrial applications.This article is protected by copyright. All rights reserved.

materials science, multidisciplinary