Abstract:Previous studies suggested that Zintl phases related to the Ca9Zn4.5− δ Sb9 (0 δ x Cu x Sb9 indicated that they could achieve an optimized zT around 0.7. Especially for Ca9Zn4.5− δ Sb9, a very recent report suggested that a high zT of 1.1 at 875 K could be obtained in combination of various secondary phases introduced by the variation of Zn contents, which provided a chemical potential to change the composition. However, to change the composition of Ca9Zn4.5− δ Sb9 is actually very difficult to implement owing to the narrow homogeneity range. In this work, with Ca substituted by big cations such as Eu2+ and Sr2+, the unit cell of Ca9Zn4.5− δ Sb9 was expanded, and similar significant enhancement on the thermoelectric performance was resulted. All syntheses were handled inside a glovebox, then the reactants were loaded in the Nb tube and arc-welded, which were enclosed in a fused silica tube. The reactions were firstly heated to 1173 K in 6 h and then maintained at this temperature for 24 h. After the homogeneity process, the furnace was slowly cooled down to 873 K at a rate of 6 K/h, followed by another dwelling for 6 hours and finally cooled down to 573 K at a rate of 10 K/h. At last, the furnace was shut down and the reactions were opened in the glovebox. The compound were fully characterized by single-crystal X-ray diffraction (SXRD) and powder X-ray diffraction(PXRD), Energy dispersive spectrometer (EDS) and Hall effect measurement, etc. Single-crystal X-ray diffraction (SXRD) proves that with the increase of Sr component, the crystal parameters are slightly increasing. Hall effect measurement show that the substitution of Ca by Eu or Sr can both lead to an obvious decreasing on the carrier (holes) concentration, and the resultant mobility for Sr/Eu-doped materials is very similar if compared by the same doping level. It is also noted that neither the carrier concentration nor the mobility seems to vary linearly with the Eu/Sr-doping contents, which means a saturated state will be eventually approached. This phenomenon is consistent with the speculation above that the changes on the properties should predominantly originate from the change of interstitial Zn content, which the size effect dominated. While the decreasing carrier concentrations as well as the increasing mobility and lattice thermal conductivity all point to a structure modification, the crystal structures of these doped materials were systematically verified through the single crystal X-ray diffraction. In conclusion, although a direct measurement on such a small composition variation is very difficult (the X-ray diffraction results prove it), the significantly reduced carrier concentration and increased mobility as well as lattice thermal conductivity can still provide some useful hints on understanding the property optimization of these materials. For material Ca8.2Eu0.8Zn4.5− δ Sb9, high figure of merit with ZT ~0.81 has been achieved at 873 K.

Preparation of copper ion doped strontium zirconate and its infrared emission characteristics

The effect of Al3+ doping on the infrared radiation and thermophysical properties of SrZrO3 perovskites as potential low thermal infrared material

Preparation and characterization of sol–gel derived copper–strontium–oxide thin films

Relationship Between Thermoelectric Properties and Infrared Emissivity of Gd-doped SrO(SrTiO3)2

Structural, morphological, and optical properties of strontium doped lead-free BCZT ceramics

Effect of dopant loading and calcination conditions on structural and optical properties of ZrO2 nanopowders doped with copper and yttrium

Investigation of the Crystal Structure, Lattice Vibration and Dielectric Property of SrZrO3 Ceramic

Infrared radiation and thermal properties of Al-doped SrZrO3 perovskites for potential infrared stealth coating materials in the high-temperature environment

Cubic phase stability, optical and magnetic properties of Cu-stabilized zirconia nanocrystals

Influence of doping elements on thermo-physical properties of co-doped strontium zirconate for potential thermal barrier coatings

Synthesis, microstructure and dielectric properties of zirconium doped barium strontium titanate obtained by solvothermal method

Preparation and characterization of CuO–ZrO2 nanopowders

Sr/Eu Cation Doping and Thermoelectric Properties of the Compound Ca9Zn4.5−δSb9 (0<Δ<0.5)

Preparation and infrared emissivities of alkali metal doped ZnO powders

Enhancement of microwave absorption properties of SrxFe12-yPr0.4o19-θ (x=0.6–1.3, y=0∼0.4) by tuning the calcination temperatures

Effect of Ca doping on the thermoelectric properties of SrCu2O2

Effect of Sr-doping on sinterability, morphology, structure, photocatalytic activity and AC conductivity of ZnO ceramics

A Study on the Relationship between the Thermoelectric Properties and Infrared Emission Performance of ZnO/SrTiO3 Composite Materials

Preparation and electrical properties of SrTiO3 ceramics doped with M2O3–PbO–CuO

Effects of Cu Ion Implantation on the Microstructure, Dielectric and Impedance Properties of SrTiO3 Ceramics Prepared by Reduction-Reoxidation Method

Effect of Sr doping on structural, morphological, optical and electrical properties of spray pyrolized CdO thin films