Tribological Properties of Polyimide Composites Modified with Diamondoid Metal–Organic Frameworks

Zihui Yu,Xianqiang Pei,Qianyao Pei,Yan Wang,Zhancheng Zhang,Yaoming Zhang,Qihua Wang,Tingmei Wang

DOI: https://doi.org/10.3390/polym16060806

IF: 5

2024-03-14

Polymers

Abstract:In this work, diamondoid metal-organic frameworks (MOFs) were efficiently prepared by sonochemical synthesis and grown on polyimide (PI), aiming to improve the anti-wear performance of the PI matrix. By introducing MOFs into the PI matrix, the free movement of PI molecular chains were restricted, and its hardness and elastic modulus were improved. It was found that the wear rate of the 3 wt.% MOFs/PI composites was reduced by 72.6% compared to pure PI at a load of 4 N after tribological testing by using a ball-on-disk tribometer. This can be attributed to the excellent load-bearing and shear resistance of the fourfold-interpenetrated diamondoid networks, in which the transition metal elements can favor the formation of transfer films. It is worth noting that the 3 wt.% MOFs/PI composites still exhibited great tribological properties under high loads or high speeds. The findings of the present study indicate that diamondoid metal-organic frameworks can be used as efficient modifiers to enhance the tribological properties of PI.

polymer science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: by introducing adamantane - type metal - organic frameworks (MOFs) into the polyimide (PI) matrix, the wear - resistant performance of PI materials is improved. Specifically, the researchers focus on how to optimize the mechanical and tribological properties of PI composites by adding different contents of MOFs, especially reducing their wear rate and improving their anti - wear ability under high - load or high - speed conditions.

The paper mentions that although pure PI has good low - temperature, high - temperature, radiation - resistance and self - lubricating properties, its friction coefficient and wear rate are relatively high, which limits its application in extreme environments. By introducing MOFs, the free movement of PI molecular chains can be restricted, thereby increasing its hardness and elastic modulus, and further improving its tribological properties. The experimental results show that when the addition amount of MOFs is 3 wt.%, compared with pure PI, the wear rate of the composite material is reduced by 72.6%, which is mainly attributed to the excellent load - bearing capacity and shear resistance of the adamantane - type network structure, in which the transition metal elements help to form a transfer film, further improving the wear - resistant performance of the material. In addition, when the MOFs content is increased to 7 wt.%, due to three - body abrasive wear, the transfer film is destroyed, and the wear - resistant performance of the composite material begins to decline. These findings indicate that adamantane - type metal - organic frameworks can be used as effective modifiers to enhance the tribological properties of PI.