Toward Unraveling the Origin of Lithium Fluoride in the Solid Electrolyte Interphase

Chuntian Cao,Travis P. Pollard,Oleg Borodin,Julian E. Mars,Yuchi Tsao,Maria R. Lukatskaya,Robert M. Kasse,Marshall A. Schroeder,Kang Xu,Michael F. Toney,Hans-Georg Steinrück

DOI: https://doi.org/10.1021/acs.chemmater.1c01744

IF: 10.508

2021-09-14

Chemistry of Materials

Abstract:The solid electrolyte interphase (SEI) is an integral part of Li-ion batteries and their performance, representing the key enabler for reversibility and also serving as a major source of capacity loss and dictating the cell kinetics. In the pervasive LiPF6-containing electrolytes, LiF is one of the SEI's major components; however, its formation mechanism remains unclear. Electrochemically, two separate reduction pathways could lead to LiF, either via direct anion reduction or electrocatalytic transformation of HF. This work aims to shed light on understanding the role played by these pathways. In a multimodal experimental and theoretical approach, we carried out operando structural characterization on an inert model single crystalline N-doped SiC working electrode during voltammetric scans in LiPF6 baseline electrolytes and complemented these with ex situ chemical characterization. These results were supplemented by cyclic voltammetry measurements using a variety of electrolyte formulations under different cycling rates as well as quantum chemical calculations and Born–Oppenheimer molecular dynamics simulations. Our results reveal that the reductive formation of LiF in these systems is likely a combined mechanism, which concomitantly involves both direct anion reduction and electrocatalytic transformation of HF. Specifically, LiF nucleates via the electrocatalytic transformation of HF followed by significant anion reduction.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.chemmater.1c01744.(Figure S1) All datasets from LP30 at 0.16 mV/s and confidence interval approach; (Figure S2) additional XPS; (Figure S3) electrochemistry for several cycles and with different scan rates; (Figure S4) electrochemistry for several cycles and with different scan rate, with current normalized by sweep rate; (Figure S5) electrochemistry for several cycles and with different scan rates, with current normalized by sweep rate, plotted with different y-axis scales; (Figure S6) all parameters from all XRR data; (Figure S7) selected XRD results from operando XRD experiment on the SiC electrode during CV; (Figure S8) electrochemistry of Li plating and stripping on SiC substrate; (Table S1) breakdown of all reactions observed over 24.0 ps trajectories; (Figure S9) BOMD snapshots; (Movies r1–r6) BOMD animations; and (Figure S10) all XRR data sets (PDF)This article has not yet been cited by other publications.

materials science, multidisciplinary,chemistry, physical