Abstract:OBJECTIVES:The study investigated the solid reactants of amorphous calcium phosphate (ACP) nanoparticles with 10-methacryloyloxydecyl dihydrogen phosphate (MDP) in ethanol-aqueous solution, and the effect of ACP-MDP suspension as a novel primer on dentin micro-tesnisl bond strengths (MTBS) prior to application of self-etch adhesives.MATERIALS AND METHODS:The ACP nanoparticles were synthesized. The solid reactants of ACP nanoparticles with MDP ethanol-aqueous solution were analyzed by TEM, SEM, XRD and AFM. After the ACP-MDP complexes were attacked by alkaline, acidic and self-etch adhesive challenges, they were analyzed with TEM. The polished mid-coronal dentin surfaces of six third molars were treated with ACP-MDP suspension, 5% MDP solution or not (served as control), and thoroughly water-sprayed. The pretreated dentin surfaces were applied with a self-etch adhesive (Clearfil S3 Bond) and placed with a composite resin (Clearfil Majesty). After 24 h, the resin-bonded samples were cut into multiple beams before the MTBS tests were performed. The failure modes were determined by a stereo-microscopy. The pretreated dentin surfaces were analyzed by SEM. The resin-dentin interfaces were analyzed with TEM.RESULTS:The ACP nanoparticles in the MDP ethanol-aqueous solution at certain molar ratio of Ca:MDP (0.12:1) could self-assemble into ACP-MDP complexes consisting of nanolayering structures. The ACP-MDP self-assembly went from ACP nanoparticles, beaded structures, and twig-like structures to networks. The ACP-MDP complexes can be resistant to adhesive challenge, but not to alkaline and acidic challenges. ACP-MDP complexes possessed a similar modulus of elasticity to dentin, and were stable at least for 3 months. Furthermore, the dentin surfaces treated with ACP-MDP suspension could significantly increase the dentin MTBS when compared with control and those treated with 5% MDP solution (P < 0.05).CONCLUSION:The ACP-MDP suspension at certain molar ratio of Ca:MDP (0.12:1) could be self-assembled into ACP-MDP complexes consisting of nanolayering structures, and could be used as a novel primer to greatly improve the dentin bond strengths.

Observation of calcium phosphate powder mixed with an adhesive monomer experimentally developed for direct pulp capping and as a bonding agent

Reconstruction of a Demineralized Dentin Matrix Via Rapid Deposition of CaF2 Nanoparticles in Situ Promotes Dentin Bonding.

Interactions of two phosphate ester monomers with hydroxyapatite and collagen fibers and their contributions to dentine bond performance

Quantitative/qualitative analysis of adhesive-dentin interface in the presence of 10-methacryloyloxydecyl dihydrogen phosphate

Effect of an Amorphous Calcium Phosphate Agent on Artificial Dentin Caries Lesions

Composite Containing Calcium Phosphate Particles Functionalized with 10-MDP

Antimicrobial activity and tightness of a DCPD-CaO-based hydraulic calcium phosphate cement for root canal filling

Chlorhexidine-loaded Poly (amido Amine) Dendrimer and a Dental Adhesive Containing Amorphous Calcium Phosphate Nanofillers for Enhancing Bonding Durability.

Bonding Durability, Antibacterial Activity and Biofilm Ph of Novel Adhesive Containing Antibacterial Monomer and Nanoparticles of Amorphous Calcium Phosphate.

Comparative evaluation of incorporation calcium silicate and calcium phosphate nanoparticles on biomimetic dentin remineralization and bioactivity in an etch-and-rinse adhesive system

Comparative Study on Adhesive Performance of Functional Monomers

Chemical and Physical Properties of Contemporary Pulp Capping Materials

Calcium Silicate and Calcium Hydroxide Materials for Pulp Capping: Biointeractivity, Porosity, Solubility and Bioactivity of Current Formulations

Nanolayering of phosphoric acid ester monomer on enamel and dentin

An in Vitro Investigation of the Mechanical-Chemical and Biological Properties of Calcium Phosphate/Calcium Silicate/Bismutite Cement for Dental Pulp Capping

Interaction of ACP and MDP and Its Effect on Dentin Bonding Performance

Effects of Phosphoric Acid Pre-Etching on Chemisorption between Enamel and MDP-Containing Universal Adhesives: Chemical and Morphological Characterization, and Evaluation of Its Potential

Effect of several additives and their admixtures on the physico-chemical properties of a calcium phosphate cement

Calcium phosphate ion clusters improve the mechanical properties and bonding strength of demineralized dentine

The roles of 10-methacryloyloxydecyl dihydrogen phosphate and its calcium salt in preserving the adhesive–dentin hybrid layer

Poly (amido amine) dendrimer and dental adhesive with calcium phosphate nanoparticles remineralized dentin in lactic acid