Calcium phosphate ion clusters improve the mechanical properties and bonding strength of demineralized dentine

Ding Yuan,Lumiao Yan,Ruitian Chen,Zhuo Chen,Ruikang Tang,Zhi Chen

DOI: https://doi.org/10.21203/rs.3.rs-2157453/v1

2022-01-01

Abstract:Abstract Objective In this laboratory study, the rapid biomimetic remineralization potential of calcium phosphate ion clusters (CPICs) on the interface between demineralized dentin and resin composite was investigated. Methods Dentin disks 1 mm thick were prepared from extracted non-carious human third molars. After acid etching, a 5 µm thick demineralized layer was obtained, sprayed with 1 mg/mL CPICs for 5 min and stored in m-SOF for 48 h. Scanning electron microscopy (SEM) was used to observe the ultrastructure of remineralized dentin treated by CPICs, and the phase transformation of the newly formed remineralized layer was determined by X-ray diffraction (XRD). A nanoindentation test was performed to evaluate the elastic modulus and microhardness of demineralized dentin. The inhibitory effect of CPICs on the activity of dentin matrix metalloproteinase was determined. Energy dispersive X-ray spectroscopy (EDS) and microcomputed tomography (micro-CT) was used to observe the bonding interface defects between the resin composite and demineralized dentin. Microtensile bond strength and failure models of bonding interface were also analyzed. Results SEM illustrated a remineralized layer of approximately 2 µm on the surface of the demineralized dentin, and the tubules of the dentin were uniformly sealed. The elastic modulus and microhardness were boosted and like those of sound dentin. In addition, have an inhibitory ability against MMP. The integrity of the bonding interface and long-term bonding strength were enhanced. CPICs transformed the failure mode into cohesive failure in the composite Conclusion CPICs greatly improved the mechanical and bonding properties of the demineralized dentine. Clinical Relevance CPICs have been shown to significantly improve the mechanical and bonding properties of demineralized dentin, which provides a new clinical treatment strategy for the demineralized dentin retained by selective caries removal technology in deep caries treatment.