Abstract:The current study highlights the corrosion consequences observed in API 5L X65 carbon steel when exposed to a marine-like environment containing carbon dioxide (CO2), in the presence of sulfate- reducing bacteria consortium (C-SRB), iron-reducing bacteria consortium (C-IRB), and a combination of both (C-SRB+C-IRB). The corrosion behaviour was assessed through the utilisation of weight loss and surface analysis techniques. The biofilms and corrosion products were characterised using field emission scanning electron microscopy (FESEM) and infinite focus microscope (IFM), respectively. The results obtained from the weight loss technique provided confirmation that in the absence of bacteria, uniform corrosion was the prevailing mechanism in the medium. The uniform corrosion rate was found to be 0.95 mm/year, which was higher than the pit penetration rate of 0.28 mm/year. The combined actions of the C-SRB+C-IRB consortium result in a synergistic impact, leading to a significantly higher rate of pit penetration compared to the individual activities of SRB. Specifically, the pit penetration rate value of 2.13 mm/year is observed, which is notably higher than the uniform corrosion rate of 0.59 mm/year. The utilisation of surface analysis techniques has shown evidence of the existence of sulfur on carbon steel samples that were subjected to exposure from the C-SRB+C-IRB consortium in a CO2 environment. This sulphur presence is believed to potentially play a role in the development of the iron sulphide (FeS) layer. FeS presence is a contributing factor to the occurrence of pit corrosion due to the SRB metabolite activities. The activities of these metabolites readily dissolve in the medium, hence altering the chemical interface properties of both the metal and the biofilm. For specimens exposed to C-SRB only, the results obtained were almost identical to exposure to the C- SRB+C-IRB consortium. However, the corrosion rate value measured for the C-SRB+C-IRB consortium was higher due to the synergistic effect of the two bacteria. In conclusion, the presence of C-SRB alone and the consortium of C-SRB+C-IRB in a CO2 environment induces the formation of pitting corrosion. The findings of this study are presumed to contribute a deep understanding of the microbiology-influenced corrosion (MIC) mechanism in CO2 environments troubling the oil and gas industry. With a better understanding of MIC, new and improved corrosion prevention strategies can be put into action.

Simulating Offshore Oilfield Conditions: Insights into Microbiologically Influenced Corrosion from a Dual Anaerobic Biofilm Reactor

Dual anaerobic reactor model to study biofilm and microbiologically influenced corrosion interactions on carbon steel

Succession of Fungal Communities and Fungal-Bacterial Interactions in Biofilm Samples Within a Multistage Bio-Contact Oxidation Reactor During the Treatment of Low-Cod and High-Salinity Produced Water

Advances in understanding biofilm-based marine microbial corrosion

Onset of microbial influenced corrosion (MIC) in stainless steel exposed to mixed species biofilms from equatorial seawater

Bibliometric Analysis of Microbiologically Influenced Corrosion (MIC) of Oil and Gas Engineering Systems

Study on the screening of marine beneficial bacteria and the inhibition of sulfate-reducing bacteria corrosion in marine oil field produced water

Responses of Microbial Community Composition to Temperature Gradient and Carbon Steel Corrosion in Production Water of Petroleum Reservoir

Microbial community profiles grown on 1020 carbon steel surfaces in seawater-isolated microcosm

Characteristics of microbiota, core sulfate-reducing taxa and corrosion rates in production water from five petroleum reservoirs in China

Simulation of the Marine Environment Using Bioreactor for Investigation of 2507 Duplex Stainless Steel Corrosion in the Presence of Marine Isolated Bacillus Vietnamensis Bacterium

A study on the microbial biocorrosion behavior of API 5 L X65 carbon steel exposed to seawater

Methanogenic Archaea and Sulfate Reducing Bacteria Induce Severe Corrosion of Steel Pipelines after Hydrostatic Testing

Characterization of bacterial communities associated with seabed sediments in offshore and nearshore sites to improve Microbiologically Influenced Corrosion mitigation on marine infrastructures

Influence of Sulfate and Iron Reducing Bacteria on Carbon Steel Corrosion in Marine Environments

Changes in microbial community in the presence of oil and chemical dispersant and their effects on the corrosion of API 5L steel coupons in a marine-simulated microcosm

Temporal Dynamics of In-Field Bioreactor Populations Reflect the Groundwater System and Respond Predictably to Perturbation

Impact and Role of Bacterial Communities on Biocorrosion of Metals Used in the Processing Industry

Accelerated corrosion of pipeline steel in the presence of Desulfovibrio desulfuricans biofilm due to carbon source deprivation in CO2 saturated medium

Exploring the influence of deposit mineral composition on biofilm communities in oil and gas systems

Diversity and Composition of Sulfate-Reducing Microbial Communities Based on Genomic Dna and Rna Transcription in Production Water of High Temperature and Corrosive Oil Reservoir